用硅烷偶联剂甲基丙烯酰氧丙基三甲氧基硅烷(MPTMS)和丙烯酸丁酯(BA)对硅土(SE)进行表面接枝改性,用傅立叶红外光谱分析了改性硅土的表面化学结构.以改性硅土与 EPDM和 PP等共混,采用动态硫化的方法制备了热塑性弹性体(TPE),考察了改性硅土对热塑性弹性体的力学性能和耐磨性能的影响.结果表明:添加改性硅土可使 TPE的 100 %定伸强度、撕裂强度和耐磨性能有所提高,但是拉伸强度有所下降.

参考文献

[1] Gessler A M .Process for Preparing a Vulcanized Blend of Crystalline Polypropylene and Chlorinated Butyl Rubber[P].US 3037954,1962-06-05.
[2] Fisher W K .Dynamically Partially Cured the Thermoplastic Blend of Monoolefin Copolymer Rubber and Polyolefin Plastic[P].US 3806558,1974-04-23.
[3] Coran A Y;Das B;Patel R P .Thermoplastic Vulcanizates of Olefin Rubber and Polyolefin Resin[P].US 4130535,1978-12-19.
[4] Coran A Y;Patel R .Rubber-thermoplastic Compositions PartⅠ.EPDM /PP Thermoplastic Vulcanizates[J].Rubber Chemistry and Technology,1980,53(01):141-150.
[5] Coran A Y;Patel R .Rubber-thermoplastic Compositions Part Ⅴ.Selecting Polymers for Thermoplastic Vulcanizates[J].Rubber Chemistry and Technology,1982,55(01):116-136.
[6] 耿海萍;朱玉俊;伍社毛 等.共混方法和设备对聚酯短纤维增强动态硫化 EPDM/PP共混型热塑性弹性体性能的影响[J].合成橡胶工业,1996,19(01):47-49.
[7] 杨华明,曹建红,敖伟琴,邱冠周.超细滑石粉填充PP的增强效应[J].中国塑料,2003(01):82-84.
[8] 蒋叙良;李长江;潘建强 .浙江硅土及其开发应用[J].浙江地质,1994,10(02):67-75.
[9] 潘建强,李长江,蒋叙良.硅土充填高聚物的性能研究[J].科技通报,1996(03):139-142.
[10] 黄俊连;韦日钦 .硅土一种极有前途的橡胶工业无机填料[J].橡胶工业,1991,38(01):526-530.
[11] 陈庆华,钱庆荣,肖荔人.EPDM/PP动态硫化热塑性弹性体的研制及应用[J].工程塑料应用,2002(05):9-12.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%