阐述了Ti基大块金属玻璃(BMG)的成分设计原则及制备方法,并对Ti基非晶合金及其部分晶化复合材料的力学性能及断裂机理进行了评述.结果表明:Ti基大块金属玻璃具有较高的断裂强度、弹性延伸率及一定的塑性延伸率,而经过部分晶化获得的非晶合金基纳米颗粒复合材料,其室温塑性获得很大的改善.在此基础上探讨了该合金目前所存在的问题、研究热点以及其应用前景.
参考文献
[1] | Tao Zhang;Akihisa Inoue .Thermal and mechanical properties of Ti-Ni-Cu-Sn amorphous alloys with a wide supercooled liquid region before crystallization[J].Materials transactions,1998(10):1001-1006. |
[2] | Tao Zhang;Akihisa Inoue .Preparation of Ti-Cu-Ni-Si-B amorphous alloys with a large supercooled liquid region[J].Materials transactions,1999(4):301-306. |
[3] | Inoue A .Stabilization of Metallic Supercooled Liquid and Bulk Amorphous Alloys[J].Acta Materialia,2000,48:279. |
[4] | Tao Zhang;Akihisa Inoue;Tsuyoshi Masumoto.Amorphous (Ti, Zr, Hf)-Ni-Cu Ternary Alloys with A Wide Supercooled Liquid Region[J].Materials Science and Engineering,1994:1423-1426. |
[5] | Inoue A;Nishiyama N .Ti-based Amorphous Alloys with A Wide Supercooled Liquid Region[J].Materials Letters,1994,19:131-135. |
[6] | Kim YC.;Bae DH.;Kim WT.;Kim DH. .Glass forming ability and crystallization behavior of Ti-based amorphous alloys with high specific strength[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,2003(1/3):242-250. |
[7] | Zhang T;Inoue A .ThermalandMechanicalPropertiesofTi-Ni-Cu-SnAmorphousAlloyswithaWideSupercooledLiquidRegionbeforeCrystallinzation[J].Materials Transactions,1998,39:1001-1006. |
[8] | Tao Zhang;Akihisa Inoue .Preparation of Ti-Cu-Ni-Si-B amorphous alloys with a large supercooled liquid region[J].Materials transactions,1999(4):301-306. |
[9] | 徐民 .具有大过冷液相区的多元铁磁性非晶合金的研究[D].中国科学院金属研究所,2002. |
[10] | Amiya K;Inoue A .Thermal Stability and Mechanical Properties of Mg-Y-Cu-M (M = Ag,Pd) Bulk Amorphous Alloys[J].Materials Transactions,2001,41:1460-1462. |
[11] | Inoue A .Preparation and Novel Properties of Nanocrystal line and Nanoquasicrystalline Alloys[J].Nanostructured Materials,1995,6:53-64. |
[12] | M. Calin;J. Eckert;L. Schultz .Improved mechanical behavior of Cu-Ti-based bulk metallic glass by in situ formation of nanoscale precipitates[J].Scripta materialia,2003(6):653-658. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%