研究了Ti-6Al-4V合金在800℃、850℃和900℃高温条件下进行拉伸试验时空气氧化对超塑性能的影响.通过光学显微镜、扫描电镜和X射线衍射分析了该钛合金氧化层的微观形貌和成分组成,并研究其在高温拉伸下的氧化机理.结果表明,高温氧化导致该合金在高温拉伸过程中表面产生氧化层,而在拉伸应力作用下氧化层断裂并向基体扩展,从而严重降低了Ti-6Al-4V合金的超塑性,但不会影响其抗拉强度及屈服强度.
参考文献
| [1] | Meier M L;Lesuer D R;Mukherjee A K .[J].Materials Science and Engineering A,1991,136:71. |
| [2] | Kim J S;Kim J H;Lee Y T et al.[J].Materials Science and Engineering A,1999,263:272. |
| [3] | Schuh C;Dunand D C .[J].Journal of Materials Research,2001,16:865. |
| [4] | Patankar S N;Escobedo J P;Field D P et al.[J].Journal of Alloys and Compounds,2002,345:221. |
| [5] | 唐兆麟 等.[J].稀有金属,1998,20(04):291. |
| [6] | Patankar S N;Yeo Thye Kwang;Tan Ming Jen .[J].Journal of Materials Processing Technology,2001,112:24. |
| [7] | Du H L;Datta P K;Lewis D B et al.[J].Corrosion Science,1994,36:631. |
| [8] | 赵宇光,周伟,秦庆东,梁云虹,姜启川.预氧化处理对钛合金抗高温氧化行为的影响[J].特种铸造及有色合金,2004(03):34-36. |
| [9] | Boettcher C .[J].Surface Engineering,2000,16:148. |
| [10] | Patankar S N;Tan M J .[J].Eng J Mater Tech,2001,123:144. |
| [11] | Evan R W;Hull R J;Wilshire B .[J].Journal of Materials Processing Technology,1996,56:492. |
| [12] | 朱日彰;何业东;齐慧滨.高温腐蚀及耐高温腐蚀材料[M].上海:上海科学技术出版社,1995 |
| [13] | Frangini S;Mignone A;Riccardis F .[J].Journal of Materials Science,1994,29:714. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%