利用热分解方法在不同温度下制备了不同Ce含量的三元涂层Ru0.3Ti(0.7-x)CexO2,通过极化曲线和交流阻抗谱测试,研究了涂层的电催化活性,通过扫描电镜对涂层表面形貌进行了观察.结果表明在涂层中引入Ce可以提高涂层阳极的电催化活性,Ce的掺入量有一个最佳比,摩尔分数为0.2～0.3时电催化性能最好;适宜的热分解温度有利于含Ce涂层阳极性能的提高,最佳温度为450℃.
参考文献
| [1] | Trasatti S .[J].Electrochimica Acta,2000,45:2377. |
| [2] | Beer H .[P].US 3632498,1972. |
| [3] | Morimitsu M.;Matsunaga M.;Otogawa R.;Tamura H. .Polarization behaviour and lifetime of IrO2-Ta2O5-SnO2/Ti anodes in p-phenolsulfonic acid solutions for tin plating[J].Journal of Applied Electrochemistry,2000(4):511-514. |
| [4] | Fujimura K;Izumiya K;Kawaashima A .[J].Journal of Applied Electrochemistry,1999,29:765. |
| [5] | Yang CH.;Wen TC.;Lee CC. .Hypochlorite generation on Ru-Pt binary oxide for treatment of dye wastewater[J].Journal of Applied Electrochemistry,2000(9):1043-1051. |
| [6] | Trasatti S;Lodi G.Electrodes of Conductive Metallic Oxides(Part B)[M].Amsterdam:Elsevier,1981:521. |
| [7] | Nidola A.Electrodes of Conductive Metallic Oxides(Part B)[M].Amsterdam:Elsevier,1981:521. |
| [8] | Watson P R;Wabner D W .[J].Journal of Catalysis,1982,74:282. |
| [9] | Brittain H G .[J].Journal of Catalysis,1983,80:334. |
| [10] | Trasatti S;Atanasoska L J D;Minevski Z S et al.[J].Materials Chemistry and Physics,1989,22:231. |
| [11] | Silava L A Da;Alves V A;Trasatti S.[J].Journal of Electroanalytic Chemistry,1997:97. |
| [12] | Faria L A .[J].Journal of Apply Electrochemistry,1996,26:1195. |
| [13] | Lo YL.;Hwang BJ. .CHARACTERIZATION OF THE ELECTROLESS NI-MO-P/SNO2/TI ELECTRODES WITH HEAT-TREATMENT FOR OXYGEN EVOLUTION IN ALKALINE SOLUTION[J].Journal of the Electrochemical Society,1996(7):2158-2164. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%