以选矿所得的天然斜锆石为原料,通过添加一定量的CaO稳定剂,经微波烧结直接制成Ca增韧部分稳定氧化锆陶瓷.微波设备采用的是自行研制的多模腔微波烧结装置,该装置频率为2.45 GHz,最大功率为3 kW.实验发现,物料在多模腔中经微波加热至约1300℃保温80 min得到部分稳定氧化锆陶瓷,其密度可达到理论密度的92.97%,抗弯强度达138.271 MPa.
参考文献
| [1] | 谢志鹏;黄勇;吴越 等.ZTA陶瓷微波烧结[J].硅酸盐学报,1995,23(01):7-12. |
| [2] | 刘一声.氧化铝和氧化锆、陶瓷的微波烧结[J].电子材料,1992(07):9-16. |
| [3] | Sutton W H .Microwave processing of ceramic materials[J].American Ceramic Society Bulletin,1989,62(02):376-386. |
| [4] | Sheppard L M .Manufacture of ceramics with microwaves the potential for economical production[J].American Ceramic Society Bulletin,1988,67(10):1656-1661. |
| [5] | Samuel J;Brandon J R .Effect of composition on the enhanced microwave sintering of alumina-based ceramic composite[J].Journal of Materials Science,1992,27(12):3259-3265. |
| [6] | Johnson D L .Microwave and plasma sintering of ceramics[J].Ceramics International,1991,17(05):295-300. |
| [7] | 周欣燕,张振涛,沙顺萍,赵璐,向蓝翔,陈宗璋,李素芳,吴振军.（ZrO2）0.96（Y2O3）0.03（Al2O3）0.01陶瓷的制备及性能研究[J].稀有金属,2007(02):187-191. |
| [8] | 王常珍.固体电解质和化学传感器[M].北京:冶金工业出版社,2000 |
| [9] | 郑文裕,陈潮钿,陈仲丛.二氧化锆的性质、用途及其发展方向[J].无机盐工业,2000(01):18-20. |
| [10] | Clark D E.Ceramic engineering and science proceedings[M].Florida:American Ceramic Society,1997 |
| [11] | 丁明桐,杜先智,陈凡,昂锋.Y-ZrO2稀土增韧陶瓷的微波烧结[J].安徽师范大学学报(自然科学版),2000(04):344-346. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%