通过加速老化试验,研究了HTPB/TDI/MAPO类聚氨酯材料的老化性能,探讨了其老化机理.实验结果显示,随老化时间的延长,HTPB胶片的表面硬度、凝胶百分数与相对交联密度均为先略微增加后明显降低的趋势.红外光谱测试结果表明,OH的伸缩振动峰强度降低,表明OH减少,这主要是由于贮存前期后固化的作用.P-N的相对吸光度值不断降低,说明P-N断裂.密封贮存条件下HTPB胶片的老化机理是后固化和降解断链.
参考文献
| [1] | 邹德荣.聚醚聚氨酯弹性体及其老化性能研究[J].合成材料老化与应用,2002(02):13-18. |
| [2] | 肖琰,魏伯荣,杜茂平.橡胶加速老化试验及贮存期推算方法[J].合成材料老化与应用,2007(01):40-43. |
| [3] | 张长生,王建华,石耀刚,丁国芳.聚氨酯耐热降解性能的研究进展[J].合成材料老化与应用,2005(02):28-32. |
| [4] | Layton L H .Chemical structural sging effects[ADA002836][R].,1974. |
| [5] | Cunliffe A V;Tod QinetiQ D A;Sevenoaks G B.Sol Fraction Measurements-A tool to study crosslinking and ageing in composite propellants and PBXs[A].Karlsruhe,Germany,2006 |
| [6] | Chevalier S;Perut C;Billon L.Antioxidant Selection Methodology for Hydroxy-Terminated Polybuadiene Type Sohd Propellants[A].Kadsruhe,Germany,1994 |
| [7] | Nagle D J;Celina M;Rintoul L et al.Infrared microspectroscopic study ofthe themao-oxidative degradation of hydroxy-terminated polybutadiene/isophorone diisocyanate polyurethane rubber[J].Polynler Degradation and Stability,2007,92(08):1446-1454. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%