以硒粉为催化剂,水合肼和过氧化氢为氧化还原引发体系,进行了常温常压下的丁腈橡胶乳液加氢反应,采用均匀设计法研究了水合肼用量、硒粉用量、过氧化氢用量、二酰亚胺凝胶抑制剂用量、反应温度以及反应时间等对丁腈橡胶氢化度的影响,并利用红外光谱对氢化产物进行了表征.实验结果表明,在适宜的反应条件下,可制得氢化度为90％的氢化丁腈橡胶.
参考文献
| [1] | 陈彩云;杨西萍 .饱和丁腈橡胶的制备[J].合成橡胶工业,1999,22(02):120-126. |
| [2] | 李少毅 .丁腈橡胶乳液加氢凝胶机理和加氢工艺的研究[D].北京化工大学,2005. |
| [3] | Wideman G .Proeess for hydrogenation of carbon-carbon bonds in an unsaturated polymer in latex form[P].USUS4452950,1984. |
| [4] | DSM N V;Her Overloon .Process of hydrogenation of carbon-carbon double of unsaturated polymer[P].WO00/9567,2000. |
| [5] | Xinwnag Lin;Qinmin Pan;Garry L.Rempel .Hydrogenation of nitrile-butadiene rubber latex with diimide[J].Applied Catalysis, A. General: An International Journal Devoted to Catalytic Science and Its Applications,2003(1/2):123-128. |
| [6] | Zhou SQ.;Bai HD.;Wang JG. .Hydrogenation of acrylonitrile-butadiene rubber latexes[J].Journal of Applied Polymer Science,2004(4):2072-2078. |
| [7] | Lin XW;Pan QM;Rempel GL .Gel formation in diimide-hydrogenated polymers[J].Journal of Applied Polymer Science,2005(4):1122-1125. |
| [8] | 王建国,周淑芹,张杰.丁腈胶乳加氢凝胶的形成及抑制[J].合成橡胶工业,2003(03):141-143. |
| [9] | Schulz, GAS;Comin, E;de Souza, RF .Hydrogenation of NBR Latex by Diimide Reduction Using Selenium Catalysts[J].Journal of Applied Polymer Science,2010(3):1390-1394. |
| [10] | SHT 1762-2008,橡胶氢化丁腈橡胶(HNBR)剩余不饱和度的测定红外光谱法[S].北京:中国石化出版社,2008. |
| [11] | 郝凤岭 .丁腈橡胶氢化反应过程中微观结构变化的红外光谱分析[J].弹性体,1997,7(03):33-35. |
| [12] | 孙荣恒;伊亨云;刘琼荪.数理统计[M].重庆:重庆大学出版社,2002:146. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%