根据损伤力学的基本原理,利用测量电阻的方法,研究了拉伸受力状态下,铁素体球墨铸铁的损伤力学特性.结果表明,当应力大于一定程度时,损伤发生,且随应力增加而逐渐增大.并得出了损伤变量分别随应力和应变而变化的规律.球墨铸铁存在着损伤阈值,其大小随球化率的提高而呈直线增大,但损伤阈值皆小于屈服强度,这一点对机械结构设计和选材具有重要参考意义.临界损伤变量与球化率的关系不大,在本试验条件下,约为0.06～0.068.
参考文献
| [1] | Lemaitre J .A continuous damage mechanics model for ductile fracture[J].ASME Journal of Engineering Materials and Technology,1985,107(01):83-89. |
| [2] | 沈真 .损伤力学及其在复合材料中的应用[J].力学进展,1985,15(02):147-161. |
| [3] | Zhang Wohua;VALLIAPPAN S .Continuous damage mechanics theory and application[J].International Journal of Damage Mechanics,1998,7(07):274-297. |
| [4] | 施明泽;林兆祥;卢锡如.脆性材料的损伤因子Dc测定[J].理化检验-物理分册,1990(04):37-38. |
| [5] | Fang H E;CHOW C L;YANG F.A method of damage mechanics analysis for solder material[J].Key Engineering Materials,1998:145-149:367-374. |
| [6] | 吕运冰 .碳钢的损伤力学特性[J].华中工学院学报,1985,36(06):113-118. |
| [7] | Bai Y L;XIA M F;KEF J.Dynamic function of damage and its implications[J].Key Engineering Materials,1998:145-149:411-420. |
| [8] | Lemaitre J;DUFAILLY J .Damage mechanics[J].Engineering Fracture Mechanics,1987,28(5/6):643-661. |
| [9] | 让·勒墨特黑.预估结构中的塑性破坏或蠕变疲劳破坏的损伤模型[J].固体力学学报,1981(04):512-525. |
| [10] | 钱志屏.材料的变形与断裂[M].上海:同济大学出版社,1989:177. |
| [11] | 姜明文.参量临界疲劳损伤因子Dc的测定[J].理化检验-物理分册,1990(02):40-41. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%