为了保证尖晶石基惰性阳极制品具有较高的体积密度和较低的气孔率,从原料粒度组成人手,在球列理论的基础上,通过实验对尖晶石颗粒级配进行了研究.实验中根据不同的产品规格,设定了4种不同的主颗粒,通过测量振实密度以寻求最佳的粒度级配.实验中先确定主颗粒与填充颗粒的质量分数和直径比,在此基础上加入不同含量的细粉以得到最佳的粒度级配.实验结果表明,主颗粒与填充颗粒的实际堆积方式与理论上球体的体心立方或密排六方堆积比较吻合,且当主颗粒、填充颗粒、细粉的质量分数分别为42%,18%,40%时,振实密度最大.
参考文献
| [1] | Donald R.Sadoway .Inert Anodes for the Hall-Heroult Cell: The Ultimate Materials Challenge[J].JOM,2001(5):34-35. |
| [2] | Kvande;Halvor.Inert electrodes in aluminum electrolysis cells[A].USA:Minerals,Metals and Materials Society,1999:369-376. |
| [3] | Pawlek R P.Inert anodes:an update[A].USA:Minerals,Metals and Materials Society,2002:449-456. |
| [4] | Olsen E;Thonstad J .Nickel ferrite as inert anodes in aluminum electrolysis:Part Ⅰ:material fabrication and preliminary testing[J].Journal of Applied Electrochemistry,1999,29(03):293-299. |
| [5] | Pawlek R P .Research ,development and potential[J].Light Metal Age,2002,60(1-2):50-55. |
| [6] | Olsen E;Thonstad.Behaviour of Nickel ferrite cermet materials as inert anodes[A].USA:Minerals,Metals and Materials Society,1996:249-257. |
| [7] | H. XIAO;R. HOVLAND;S. ROLSETH;J. THONSTAD .Studies on the Corrosion and the Behavior of Inert Anodes in Aluminum Electrolysis[J].Metallurgical Transactions.B.Process Metallurgy,1996(2):185-193. |
| [8] | 于先进;邱竹贤;金松哲 .铝电解用惰性阳极材料研究的发展概括[J].淄博学院学报(自然科学与工程版),1999,1(01):55-60. |
| [9] | 曾光延.材料成型加工工艺与设备[M].北京:化学工业出版社,2001:56-57. |
| [10] | 童芳森;许斌;李哲浩.炭素材料生产问答[M].北京:冶金工业出版社,2002:86-88. |
| [11] | 黄辉.颗粒级配技术及其在含能材料中的应用[J].含能材料,2001(04):161-164. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%