研究了淬火温度、冷却方式、回火温度和回火次数对高速钢轧辊组织和性能的影响.结果表明,油冷条件下,淬火温度低于1050℃,随着温度升高,硬度升高,超过1100℃,硬度反而降低.盐浴冷却(盐冷)和空冷条件下,淬火温度对硬度影响结果相似,但获得最高硬度的淬火温度高于油冷时的淬火温度.回火温度低于350℃,高速钢硬度变化不明显,超过475℃,随回火温度升高,硬度升高,并在525℃达到最高值,继续提高回火温度,硬度降低.二次回火后硬度变化不大,三次回火后,硬度反而降低.空冷高速钢轧辊,淬透性差;油冷高速钢轧辊易出现裂纹;盐冷高速钢轧辊,具有优良的淬透性,不易出现裂纹,辊面硬度高,硬度均匀性好,耐磨性好.
参考文献
[1] | M.A. de Carvalho;R.R. Xavier;C. da Silva Pontes Filho .Microstructure, Mechanical Properties and Wear Resistance of High Speed Steel Rolls for Hot Rolling Mills[J].Iron & Steelmaker,2002(1):27-32. |
[2] | E. J. Kerr .High speed steel work rolls at dofasco[J].Iron & Steelmaker,2000(1):27-30. |
[3] | Okabayashi A;Morikawa H;Tsujimoto Y .Development and characteristics of high speed steel roll by centrifugal casting[J].SEAISI(South East Asia Iron and Steel Institute) Quarterly,1997,26(04):30-40. |
[4] | Biggi A;Ippoliti A;Molinari A.Hot strip mill work roll development[A].,1998:419-426. |
[5] | Jung Ho Lee;Jun cheol Oh;Joon Wook Park .Effects of Tempering Temperature on Wear Resistance and Surface Roughness of a High Speed Steel Roll[J].ISIJ International,2001(8):859-865. |
[6] | 刘佐仁.淬火温度对高速钢力学性能的影响[J].钢铁,2001(07):54-57,67. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%