研究工业拟薄水铝石的胶溶过程的工艺参数及其胶体颗粒表面的特性.测定了以稀硝酸为胶溶剂的酸分散指数,在n(H+)/n(AlOOH·nH2O)=0.097时拟薄水铝石可以完全胶溶,所得到的溶胶pH值为3.4,TEM观察胶粒为网联的近球形,大小约为20～50 nm.通过胶溶过程中电导率的变化和胶体的红外光谱分析,间接表征了胶溶过程中拟薄水铝石胶粒的表面基团的变化.基于多核配合物平衡浓度与pH值的关系分析了胶核形成机理,对胶团的表面电荷特性和双电层结构进行了讨论.
参考文献
| [1] | YOLDASE .Aluminasolpreparationfromalkoxide[J].Ceramic Bulletin,1975,54:289-290. |
| [2] | YangQ;Troczynski T.Composite alumina sol-Gel ceramics[A].at 100th annul convention of American Ceramic Society Cincinnati,May,1998 |
| [3] | PrahakaranK;Ananthakumar S .Gelcastingofaluminausingbohmiteasabinder[J].Eu Ceram Soc,1999,19:2875-2881. |
| [4] | YOLDASE.Ultrastructure processing of advanced ceramics[M].NewYork:Wiely,1988:333-345. |
| [5] | GiselmannMJ;ersonMA .EffectofionicstrengthonboehmiteHydrogelformation[J].Journal of the American Ceramic Society,1989,72:980-985. |
| [6] | 熊国兴;赵宏宾.溶胶-凝胶制备技术与新型催化剂材料Ⅰ[J].石油化工,1994:656-662. |
| [7] | raceR;Matijevic E .Aluminumhydrousoxidesols:Ⅰ[J].Inorganic and Nuclear Chemistry Letters,1973,35:3691-3705. |
| [8] | MilonjicSK .Colloidparticlesandadvancematerial[J].Materials Science Forum,1996,214:197-204. |
| [9] | PetkovicMDj;Milonjic S K .Stabilityofcolloidaluminainthepresenceofvariousinorganicanions[J].Bulletin of the Chemical Society of Japan,1995,68:2133-2136. |
| [10] | Petrovic R.;Milonjic S.;Jokanovic V.;Kostic-Gvozdenovic L. Petrovic-Prelevic I.;Janackovic D. .Influence of synthesis parameters on the structure of boehmite sol particles[J].Powder Technology,2003(1/3):185-189. |
| [11] | 高志贤;程昌瑞 .拟薄水铝石酸分散性能的研究[J].石油炼制与化工,1999,23(10):16-19. |
| [12] | 罗玉长.拟薄水铝石结构的演化[J].现代技术陶瓷,1997(04):7-11. |
| [13] | 罗玉长.拟薄水铝石结构的演化[J].轻金属,2001(02):10-13,26. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%