以C-Mn钢SS400为研究对象,在Gleeble-1500热模拟试验机上进行了热模拟实验,测得了试验钢静、动态CCT曲线.从CCT曲线可以看出,未变形时试验钢奥氏体向铁素体开始转变温度在800～690℃之间,变形后在810～710℃之间,变形提高了Ar3点.当冷却速度比较低时(0.2～5℃/s),变形奥氏体转变后室温组织的维氏硬度值低于未变形奥氏体转变后的室温组织维氏硬度值,而当冷却速度比较高时(5～20℃/s),趋势正好相反;变形后淬火试验结果表明应变量为0.4、变形速率为1/s 时,试验钢在820℃时已经发生形变诱导铁素体相变.随着应变量的增大和变形温度的降低,原奥氏体晶界的铁素体量增多.
参考文献
| [1] | P.D.Hodgson;M.R.Hickson;R.K.Gibbs .ULTRAFINE FERRITE IN LOW CARBON STEEL[J].Scripta materialia,1999(10):1179-1184. |
| [2] | MatsumuraY;Yada H .Evolutionofultrafineferriteinhotsuccessivedeformation[J].Transactions of the Iron and Steel Institute of Japan,1987,27:492. |
| [3] | 田志凌,何长红,张晓牧,邹刚,屈朝霞.400MPa级超细晶粒钢的焊接[J].焊接学报,2001(06):1-3. |
| [4] | SeoDH;Choi J K;Choo W Y.Ferrite grain refinement by multi-pass rolling at intercritical temperature in low carbon steel[A].Chandra T,Las Vegas,2000 |
| [5] | Hua Ding;Haitao Zhang;Dengfeng Pei;ZhaodonWang;Xianghua Liu.Study on Mechanical Properties and Microstructures of Super SS400 Steel[A].,2001-01-13:141. |
| [6] | 杜林秀,刘相华,王国栋.低碳钢应变诱导铁素体相变研究中的淬火问题[J].金属学报,2002(02):196-202. |
| [7] | 孙新军 .微合金钢变形诱导铁素体相变的研究[D].钢铁研究总院,2003. |
| [8] | 杜林秀 .低碳钢变形过程及冷却过程的组织演变与控制[D].东北大学,2003. |
| [9] | 董瀚,孙新军,刘清友,翁宇庆.变形诱导铁素体相变现象与理论[J].钢铁,2003(10):56-67,55. |
| [10] | 崔忠圻.金属学与热处理[M].北京:机械工业出版社,1988:214-218. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%