研究了GH4586A合金在750℃、800℃长期时效过程中室温拉伸性能与组织变化的关系.利用扫描电镜对合金显微组织进行了观察;利用透射电镜对析出相进行了鉴定;通过物理化学相分析方法定量分析了长期时效过程中合金中相的质量分数.结果表明,该合金在750～800℃时效有μ相和σ相析出,并且随时间延长数量增加;在750～800℃长期时效过程中M23C6碳化物析出.M23C6主要在晶界析出且其析出量受时效温度及时间的影响;合金在750℃、1 500 h之内使用,强度和塑性可以匹配,超过1 500 h后由于μ相和σ相析出量明显增多,塑性迅速下降,合金不能作为转动件使用.
参考文献
| [1] | XIE S S;Pan X F;Wang T L et al.Effects of microstructure on fatigue crack growth behavior in Ni-base supperalloy GH586[J].Acta Metalluraica,1999,12(03):267-272. |
| [2] | XIE S S;Ma S S;Yang H C .Effect of heat treatments on grain sizes and 760 ℃ tensile strength in Ni-base alloy GH141[J].Nonferrous Metallurgy and Materials International Symposium,1996,9:565-569. |
| [3] | Lei Wang;Tong Cui;Junying Lu .Low-Cycle Fatigue Fracture Behavior of Superalloy GH4586 at Elevated Temperature[J].Materials Science Forum,2004(Pt.1):337-340. |
| [4] | Shuangqun Zhao;Xishan Xie;Gaylord D. Smith .Microstructural stability and mechanical properties of a new nickel-based superalloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):96-105. |
| [5] | 郭士文,张玉锁,童开峰,杨洪才.镍基高温合金长期时效后γ′相长大动力学[J].东北大学学报(自然科学版),2003(06):576-579. |
| [6] | Sims T;Stoloff S;Magel C.SuperalloysⅡ[M].New York:John Wiley & Sons,1987:259-284. |
| [7] | Dahlen M;Fischmeister H.Carbide precipitation in superalloys[A].Ohio,USA ASM:Metals Park:449-454. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%