采用连续铸挤工艺生产Al-Mg-Sc合金线材.对Al-Mg-Sc合金线材质量的影响因素:合金化工艺、铸挤轮转速、浇注温度、冷却水流量等进行了研究.结果表明:采用合理的熔炼工艺,在铸挤轮速度15 r/min,冷却水流量5L/min,熔体浇注温度720~730℃的情况下,线材表面质量好,气孔少.320℃人工时效3h,细小析出相Al3Sc粒子弥散分布在铝基体中.
参考文献
[1] | S. Lathabai;P.G. Lloyd .The effect of scandium on the microstructure, mechanical properties and weldability of a cast Al-Mg alloy[J].Acta materialia,2002(17):4275-4292. |
[2] | Davydov V G;Rostova T D;Zakharov V V et al.Scientific principles of making an alloying addition of scandium to aluminum alloys[J].Materials Science and Engineering,2003,280(01):30-36. |
[3] | Riddle Y W;Sanders T H .A study of coarsening,recrystallization,and morphology of microstructure in Al-Sc-(Zr) -Mg Alloy[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,2004,35A(01):341. |
[4] | 杨遇春.大有作为的含钪铝合金[J].金属世界,2004(01):34-35. |
[5] | Yelagin V I;Zakharov V.The effect of scandium onstructure and properities of Al-Zn-Mg Alloy[J].Izvestiya AN SSSR Metally,1983(04):180-183. |
[6] | Vinogradov A.;Washikita A.;Kitagawa K.;Kopylov VI. .Fatigue life of fine-grain Al-Mg-Sc alloys produced by equal-channel angular pressing[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):318-326. |
[7] | K. B. HYDE;A. F. NORMAN;P. B. PRANGNELL .THE EFFECT OF COOLING RATE ON THE MORPHOLOGY OF PRIMARY Al_3Sc INTERMETALLIC PARTICLES IN Al-SC ALLOYS[J].Acta materialia,2001(8):1327-1337. |
[8] | 潘青林,尹志民,邹景霞,陈显明,张传福.微量Sc在Al-Mg合金中的作用[J].金属学报,2001(07):749-753. |
[9] | 张迎晖,孝云祯,马宏声.微量元素Sc对工业纯铝再结晶的影响[J].中国有色金属学报,1998(01):85-88. |
[10] | 潘青林,尹志民,高拥政,张永红,左铁镛.Al-Mg-Sc合金的再结晶[J].中国有色金属学报,1998(03):427-430. |
[11] | 陈彦博 .铝材连续铸挤成形的实验研究与数值模拟[D].东北大学,2002. |
[12] | 王顺成,陈彦博,温景林.连续铸挤生产Al-Sr中间合金线材工艺研究[J].轻合金加工技术,2003(03):19-22. |
[13] | 周天国,温景林,王顺成.6201电工铝合金线材连续铸挤工艺研究[J].轻合金加工技术,2004(05):9-11. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%