为含钒钢渣设计富钒相,使钢渣中的钒主要富集于所设计的富钒相中.中国马钢的钢渣和瑞典SSAB的钢渣是本研究使用的样本.尽管炉渣的来源和化学组成各不相同,但是可以发现其矿物组成大致相似,而且无法仅仅通过对炉渣的热处理来实现钒的富集.本文根据钒和炉渣的基本物理化学性质设计了两种适合于作为富钒相的矿物:溶有w(Si)＜3%的3CaO·V2O5和3CaO·P2O5的固溶体以及另外一种w(Si)约10%的由3CaO·2SiO2,3CaO·V2O5和3CaO·P2O5的组成的矿物.通过添加SiO2对炉渣的化学成分进行调整,在炉渣中得到了所设计的富钒相,且炉渣中超过2/3的钒富集于其中.本研究为钢渣中的钒提出了一种新的回收利用途径.
参考文献
| [1] | Selin R.Vanadium in Ore-based Iron and Steelmaking[M].An LKAB Monograph by Roger Selin,2000 |
| [2] | Zhou jiacong.Development of China Vanadium Industry[A].Westerham,Kent,England:VANITEC,2000:7-14. |
| [3] | Perrine Chaurand;Jerome Rose;Jeremie Domas;Jean-Yves Bottero .Speciation of Cr and V within BOF steel slag reused in road constructions[J].Journal of Geochemical Exploration: Journal of the Association of Exploration Geochemists,2006(1/3):10-14. |
| [4] | R. R. Moskalyk;A. M. Alfantazi .Processing of vanadium: a review[J].Minerals Engineering,2003(9):793-805. |
| [5] | I. N. Monakhov;S. V. Khromov;P. I. Chernousov .THE FLOW OF VANADIUM-BEARING MATERIALS IN INDUSTRY[J].Metallurgist,2004(7/8):381-385. |
| [6] | Sui Z;Zhang L;Lou T.Green Technology to Recovery Value Metal Compounds from Molten Slags[A].San Diego,California-USA,2003 |
| [7] | Hubert PreBlinger;Kurt O. Klepp .Vanadium in converter slags[J].Steel Research,2002(12):522-525. |
| [8] | ONO H .Removal of Phosphorus from LD Converter Slag by Floating Separation of Dicalcium Silicate during Solidification[J].Tetsu-to-Hagane (Journal of the Iron and Steel Institute of Japan),1980,66(09):1317-1326. |
| [9] | Bergmann A .Representation of Phosphorus and Vanadium Equilibria between Liquid Iron and Complex Steelmaking Type Slags[J].Transactions of the Iron and Steel Institute of Japan,1988,28(11):945-951. |
| [10] | Werme A .Distribution of Vanadium between SiO2 Rich Slags and Carbon Saturated Liquid Iron[J].Steel Research International,1988,59(01):6-15. |
| [11] | Liang Yu;Yuan-chi Dong;Liaosha Li et al.Existence of a solid solution between 3CaO@V2O5 and 3CaO@P2O5[J].M & M trans B,2006,37B(06):1097-1099. |
| [12] | L. Yu;Y.-C. Dong;G. Z. Ye .Concentrating of vanadium oxide in vanadium rich phase(s) by addition of SiO_2 in converter slag[J].Ironmaking & Steelmaking: Products and applications,2007(2):131-137. |
| [13] | Wolff Pde .PDF-2 Data Base 1996[DB].International Centre for Diffraction Data |
| [14] | Macicek J .PDF-2 Data Base 1995[DB].International Centre for Diffraction Data |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%