The effects of the retrogression temperature and time of retrogression and re-aging heat treatment(RRA) on the hardness and electrical conductivity of Al-6.1Zn-2.6Mg-1.6Cu aluminum alloy were studied. Samples were pre-aged at 120℃ for 24h as the first-stage treatment. Then, retrogression was performed at a temperature range of 170~250℃ for times of between 1min and 180min, followed by re-aging at 120℃ for 24h. Hardness (H) and electrical conductivity (EC) measurements were used to characterize the samples after RRA treatment. Analysis of the results shows: (1)The re-aging treatment at 120℃ for 24 h increases both H and EC of the retrogressed alloy in the RRA process;(2) RRA with retrogression at higher than 200℃ result in EC higher than that of peak-aged, but H lower; The change of H and EC with respect to retrogression temperature (T) and time (t) can be seen as functions of H (t) = H0+A1e(-t/s) ,EC(t) =A(1-e(-k·(t-Xc)));(3) RRA treatments with retrogression at 190℃ for 4~30min result in H and EC which are both higher than those of the peak-aged temper, and retrogression at 190℃for 30min is the industrial application that yields H of 190 HV and EC of 33.5%IACS.
参考文献
[1] | Cina B .Reducing the susceptibility of alloy[P].US 13856584,1974. |
[2] | Oliveira A F;de Barros M C .The Effect of RRA on the Strength and SCC Resistance on AA7050 and AA7150 Aluminum Alloys[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2004,379:321-326. |
[3] | Park J K;Ardell A J .Effect of Retrogression and Reaging Treatments on the Microstructure of Al-7075-T651[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1984,15A(08):1531-1543. |
[4] | Nguyen Cong Danh .A TEM study of Microstructural Changes during Retrogression and Reaging in 7075 Aluminum Alloy[J].Metallurgical Transactions,1983,14A:1843-1850. |
[5] | Hall B Mathew;Martin J W .The Effect of Retrogression Temperature on the Properties of an RRA (Retrogressed and re-aged) 7150 Aluminum Alloy[J].Zeitschrift fur Metallkunde,1994,85(02):134-139. |
[6] | F. Viana;A. M. P. Pinto;H. M. C. Santos;A. B. Lopes .Retrogression and re-ageing of 7075 aluminium alloy: microstructural characterization[J].Journal of Materials Processing Technology,1999(0):54-59. |
[7] | Antonio Baldantoni .On the Microstructural Changes during the Retrogression and Re-aging of 7075 Aluminum Alloys[J].Materials Science and Engineering,1985,72:L5-L8. |
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%