利用扫描电镜组织观察、电子探针定量成分分析以及X射线衍射结构分析对Mg-Zn-Nd系富Mg角300℃的局部相平衡进行了研究.结果表明,在Mg-Zn-Nd系富Mg角存在一个成分(摩尔分数)范围为Mg:58.3%~63.9%,Zn:28.2%~33.6%,Nd:7.9%~8.3%的三元化合物T-2相,和成分范围为Mg:25.9%~30.3%,Zn:44.6%~48.5%,Nd:25.1%~25.6%的三元化合物T-3相.300℃时αMg相与T-2相之间存在稳定的两相平衡,而且αMg相还与T-2和T-3相之间存在稳定的三相平衡.
参考文献
[1] | Qiang Li;Qudong Wang;Yingxin Wang .Effect of Nd and Y addition on microstructure and mechanical properties of as-cast Mg-Zn-Zr alloy[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2007(1/2):115-123. |
[2] | Sugiyama K;Yasuda K;Ohsuna T et al.The structures of hexagonal phases in Mg-Zn-RE (RE=Sm and Gd) alloys[J].Zeitschrift für Kristallographie,1998,213:537-543. |
[3] | Wei LY.;Westengen H.;Dunlop GL. .SOLIDIFICATION BEHAVIOUR AND PHASE CONSTITUENTS OF CAST MG-ZN-MISCH METAL ALLOYS[J].Journal of Materials Science,1997(12):3335-3340. |
[4] | 郝士明.镁的合金化与合金相图[J].材料与冶金学报,2002(03):166-170,202. |
[5] | Villars P;Prince A;Okamoto H.Handbook of Ternary Alloy Phase Diagrams[M].ASM International,1997 |
[6] | Massalski T B;Okamoto H;Subramanian P R.Binary Alloy Phase Diagrams,Second Edition Plus Updates[M].ASM International,1996 |
[7] | Drits M E;Padezhnova E M;Miklina N V.The combined solubility of Neodymium and Zinc in solid Magnesium[J].Izvestiyaakademii Nauk SSSR Metally,1974(03):143-146. |
[8] | Petrovoj L A .Mg-Nd-Zn phase diagram.diagrammy sostoyaniya Metallicheskikh system[J].N.V.Ageeva,Viniti,Moscow,1985,30(02):598-599. |
[9] | 黄明丽,李洪晓,杨金艳,任玉平,丁桦,郝士明.Mg-Zn-Nd合金中的低Nd三元化合物T1相的研究[J].金属学报,2008(04):385-390. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%