对含铌Si-Al-Mn TRIP钢在800℃两相区退火和400℃贝氏体区等温处理,试样进行了力学和成形极限图(FLD)实验.分析了常规力学参数对成形极限平面应变特征点(FLD0)的影响.结果表明,实验钢的FLD0值为59%,表现出良好的成形性;随着延伸率δ、强塑积(σb×δ)、应变硬化指数n和塑性应变比r值的上升,FLD0具有上升的趋势.n值对FLD0的影响最为显著,r值对FLD0的影响较小.
参考文献
[1] | Ushilda K .Rencent developments in steel sheets[J].Seandinavian Metall,1999,28:33-39. |
[2] | 景财年,王作成.TRIP-相变诱发塑性钢的研究进展[J].特殊钢,2004(04):1-5. |
[3] | Lee C G;Kim S J;Song B H et al.Effect of heat treatment ON formability in 0.15C-1.5Si-1.5Mn muhiphase cold-rolled steel sheet[J].Metals and meterials International,2002,8(05):435-441. |
[4] | Jacques P;Fume Q;Pardoen T et al.On the role of martensitie transformation on damage and cracking resistance in TRlP-assisted mulfiphase steels[J].Acta mater,2001,49:139-152. |
[5] | Lee C G;Kim S J;Song B H et al.Effect of heat treatment on formability in 0.15C-1.5Si-1.5Mn muhiphase cold-rolled steel sheet[J].Metals and meterials International,2002,8(05):435-441. |
[6] | 符仁钰,苏钰,李麟,张梅.Si-Mn系TRIP钢FLD及断裂机理的研究[J].汽车工艺与材料,2004(06):75-77. |
[7] | Hiwatashi S;Hatakeyama T;Ushieda K et al.Numerical analysis of stiffness in sheet steel products based on crystal anisotropy[J].Materials Science Forum,1994,157:585-1592. |
[8] | Sakuma Y;Kimura N;Itami A et al.Next-generation hishstrength sheet steel utilizing transformation@induced plasticity (TRIP)effeet[J].NIPPON STEEL TECHNICAL REPORT,1995,64:20-25. |
[9] | Lee C G;Kim S J;Song B H et al.Effect of heat treatment on formability in 0.15C-1.5Si-1.5Mn muhiphase cold-rolled steel sheet[J].Metals and meterials International,2002,8(05):435-441. |
[10] | 张梅,李麟,符仁钰,万紫.0.11C-0.6Si-1.6Mn相变诱发塑性(TRIP)钢的成形性和可焊性[J].金属热处理,2006(04):39-42. |
[11] | 康永林.现代汽车板的质量控制与成形性[M].北京:冶金工业出版社,1999:25-252. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%