采用俄罗斯UVN 0.5D2I离子束辅助电弧离子镀沉积设备,对高速钢W18Cr4V基材表面进行氮离子束轰击,研究了氮离子束轰击能量对表面形貌、相结构及显微硬度的影响.研究表明:氮离子束轰击后基材表面原有划痕消失,表面趋于光滑.表面层出现(Fe,Cr),CrN,Cr2N和FeN相;随着氮离子束轰击能量的增加,(Fe,Cr)相结构未发生变化,CrN(111)衍射峰逐渐增强,Cr2N(211)衍射峰逐渐减弱;FeN(210)衍射峰先增强而后消失,出现Fe2N相.氮离子束轰击后的表面显微硬度由原来的900HV0.01升高到1 230 HV0.01.
参考文献
| [1] | Rickerby D S;Bull S J;Robertsson T et al.The role of titanium in the abrasive wear resistance of physically vapour-deposited TiN[J].Surface and Coatings Technology,1990,41:63. |
| [2] | Sundgren J E;Hentzell H T G.A review of the present state of art in hard coatings grown from the vapor phase[J].Journal of Vacuum Science and Technology,1986:2259. |
| [3] | Chen Y I;Duh J G .TiN coatings on mild steel substrates with electroless nickel as an interlayer[J].Surface and Coatings Technology,1991,48:163. |
| [4] | Klutha O;Recha B;Houben L et al.Texture etched ZnO:Al coated glass substrates for silicon based thin film solar cells[J].Thin Solid Films,1999,351:247. |
| [5] | Larsson M;Bromark M;Hedengvist P et al.Deposition and mechanical properties of multilayered PVD Ti-TiN coatings[J].Surface and Coatings Technology,1995,76:202. |
| [6] | Pan W L;Yu G P;Huang J H .Mechanical properties of ion-plated TiN films on AISI D2 steel[J].Surface and Coatings Technology,1998,110:111. |
| [7] | 熊仁章,夏立芳,白羽,雷廷权.TiAlN/Ti多元复合涂层的界面结构[J].材料科学与工艺,2000(02):55-57. |
| [8] | 宋贵宏,郑静地,刘越,孙超.TiAl过渡层对电弧离子镀沉积TiAlN膜层的影响[J].人工晶体学报,2004(03):422-427. |
| [9] | 徐信夫;翟乐恒;张建华.在空心阴极离子镀膜机中进行的离子渗氮的探索[M].北京:中国工业出版社,1992:12. |
| [10] | 郭铮匀.钢的氮化[M].北京:国防工业出版社,1979 |
| [11] | 夏立芳;高彩桥.钢的渗氮[M].北京:机械工业出版社,1989 |
| [12] | 刘金声.离子束沉积薄膜技术及应用[M].北京:国防工业出版社,2003:6. |
| [13] | 张通和;吴瑜光.离子束表面工程技术与应用[M].北京:机械工业出版社,2005:1. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%