By using different particle size of fused white corundum (<74 μm, 74～147 μm, >147 μm), flake graphite, solid resin, commercial alcohol, zirconia (calcium oxide as stabilizer) as the raw materials, Al2O3-C samples with the length of 850 mm, inner (alumina-graphite) diameter of 50 mm and outer (zirconium) diameter of 85 mm were prepared by cold isostatic compaction pressed at 160 MPa after prilling in granulator. An electric field was applied to Al2O3-C refractory and the effect of current intensity (0.5 A, 1 A and 5 A) on slag erosion resistance was investigated in this paper. The results show that with the increasing of current intensity, the thickness of build-up in cathode increases significantly. CaO·6Al2O3, a high melting point compound generated on the surface of slag line, decreases the slag erosion rate of Al2O3-C refractory dramatically.
参考文献
| [1] | 杨红,尹国祥,孙加林.提高ZrO2-CaO-C浸入式水口抗Al2O3附着性能的研究[J].材料与冶金学报,2008(02):89-93. |
| [2] | 马北越,朱强,于景坤.铝碳质材料和镁铝尖晶石材料表面氧化铝附着的研究[J].矿冶,2007(03):39-42,25. |
| [3] | 段锋,平增福,蒋明学,李庭寿,高云琴.浸入式水口Al2O3附着堵塞机理及防止办法[J].耐火材料,2004(03):204-207. |
| [4] | Jonas S;Nadachowski F;Szwagiercaak D .A new non-silicate refractory of low thermal expansion[J].Ceramics International,1998,24(03):211-216. |
| [5] | J.D. Lavers;Laszlo Kadar .Application of electromagnetic forces to reduce tundish nozzle clogging[J].Applied mathematical modelling,2004(1):29-45. |
| [6] | 刘建伟,王启明,成小龙.浸入式水口自动变渣线工艺的应用[J].炼钢,2007(01):11-13. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%