研究了锰含量(质量分数)为23.8%的低碳高锰钢的力学行为和组织演变,并对其强化机制进行了探讨.结果表明:23.8%Mn TRIP/TWIP钢的屈服强度约为300 MPa,抗拉强度可达610 MPa,断裂延伸率可达到63%.实验钢拉伸变形呈连续屈服,其应变硬化指数n值约为0.48.该钢在变形初期的强化机制以应变诱发孪生为主,变形后期出现应变诱发马氏体相变.位错与形变孪晶、马氏体之间的相互作用也对强度的增加做出贡献.
参考文献
| [1] | Grassel O.;Frommeyer G.;Meyer LW.;Kruger L. .High strength Fe-Mn-(Al, Si) TRIP/TWIP steels development - properties - application[J].International Journal of Plasticity,2000(10/11):1391-1409. |
| [2] | Frommeyer G;Brux U .Microstructures and mechanical properties of high-strength Fe-Mn-Al-C light-weight TRIPLEX steels[J].Steel Research International,2006,77(9-10):627-633. |
| [3] | Rintaro Ueji;Kenji Harada;Noriyuki Tsuchida;Kazutoshi Kunishige .High Speed Deformation of Ultrafine Grained TWIP Steel[J].Materials Science Forum,2007(1):107-110. |
| [4] | 米振莉,唐荻,严玲,郭锦.高强度高塑性TWIP钢的开发研究[J].钢铁,2005(01):58-60. |
| [5] | Yang P;Xie Q;Meng L;Ding H;Tang Z .Dependence of deformation twinning on grain orientation in a high manganese steel[J].Scripta materialia,2006(7):629-631. |
| [6] | 李卫,唐正友,王玫,丁桦,杨平.高锰奥氏体TRIP/TWIP钢的组织和力学性能[J].钢铁,2007(01):71-75. |
| [7] | DING Hua,TANG Zheng-You,LI Wei,WANG Mei,SONG Dan.Microstructures and Mechanical Properties of Fe-Mn-(Al, Si) TRIP/TWIP Steels[J].钢铁研究学报（英文版）,2006(06):66-70. |
| [8] | 米振莉,唐获,江海涛,代永娟,王海全.Fe-28Mn-3Si-3Al TWIP钢变形过程中的孪晶观察[J].钢铁,2007(12):73-76. |
| [9] | 周小芬,符仁钰,苏钰,李麟.Fe-Mn-C系TWIP钢的拉伸应变硬化行为研究[J].钢铁,2009(03):71-74. |
| [10] | 熊荣刚,符仁钰,黎倩,张梅,李麟.TWIP钢的拉伸应变硬化行为[J].钢铁,2007(11):61-64. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%