对于溶液共沉淀法制备镍铁尖晶石前躯粉体的工艺进行了探索研究.以Fe( NO3)3和Ni( NO3)2的混合溶液为反应物,以碳酸钠为沉淀剂进行共沉淀反应；通过正交试验确定了在共沉淀过程中影响共沉淀粒度诸因素的主次顺序依次为:反应温度、搅拌速度、沉淀剂浓度、金属离子浓度；并通过反应温度和沉淀剂浓度对产率的影响试验,最终得到共沉淀反应沉淀的最佳条件.对于所制得的镍铁尖晶石陶瓷粉体检测结果表明:溶液共沉淀法得到的镍铁尖晶石前躯体粉末具有纯度高、粒度细的特点,并且制备出的镍铁尖晶石陶瓷材料的强度显著提高.
参考文献
| [1] | Singer J;Fielder W L .Corrosion testing of candidates for the alkaline fuel cell cathode[J].Journal of Power Sources,1990,29(3-4):443. |
| [2] | Papadatos K;Shelstad K A.Catalyst screening using a stone DTA apparatus 1.oxydation of toluene over cobalt metal-oxide catalysts[J].Journal of Catalysis,1973(281):116. |
| [3] | Kato H;Sano T;Wada Y.Methanation of the oxygen deficient Ni ferrite under dynamic conditions[J].Journal of Materials Science,1995(30):6350-6354. |
| [4] | Massahiro Tabata;yoshikazu Nishida;Tatsuya Kodana.CO2 decomposition with oxygen-deficient MnO ferrie[J].Journal of Materials Science,1993(28):971-974. |
| [5] | Avakyan P B;Nersisyan E L;Nersesyan M D.Third international sympposium on self- propagating high -temperature synthesis[M].China:Wuhan,1995 |
| [6] | 姜继森;高濂;郭景坤 .固相法合成铁氧体纳米粒子[J].无机材料学报,1998,13(03):415-418. |
| [7] | 刘锦淮,焦正,张鉴,余增亮.纳米气体敏感材料的喷射共沉淀法制备及特性[J].微纳电子技术,2003(06):22-25,42. |
| [8] | 佘维清,丘泰.共沉淀法制备锰锌铁氧体微粉的研究[J].电子元件与材料,2009(03):53-56. |
| [9] | 朱林彦,张平,徐明霞.共沉淀法制备纳米铝酸锶长余辉发光粉体及其发光性能研究[J].稀有金属材料与工程,2008(z1):793-796. |
| [10] | 张小会 .喷雾热解法合成镁铝尖晶石纳米粉末的制备与表征[D].西安建筑科技大学,2004. |
| [11] | 周玉.陶瓷材料学[M].哈尔滨:哈尔滨工业大学出版社,1995:67-69. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%