以FeSO4*7H2O和NiSO4*7H2O为原料，首先制备出颗粒细小的碱式碳酸盐前驱体，在300～700℃焙烧1h后，制备出铁酸镍纳米晶，粒径为8～54nm，粒度均匀。通过测量它的比饱和磁化强度σs与比表面积Sa，得出经验公式σs(Sa)=σs(∞)(1-aSa)，运用非共线磁结构理论很好地解释了上述经验公式，并得到纳米晶的非共线表面层的厚度。
A basic carbonate precursor with very fine particles was synthesied by using FeSO4*7H2O and NiSO4*7H2O, and NiFe2O4 nanocrystallites were then obtained by calcining the precursor. The results of XRD and TEM analysis show the NiFe2O4 nanocrystallites with spherical shape are even, and their average diameters increase from 8nm to 54nm when the precursor is calcined at 300—700℃ for 1h. Their specific saturation magnetization σs and specific surface area Sa were measured. A empirical formula σs(Sa)=σs(∞)(1-aSa)was obtained which can be interpreted very well by a noncollinear magnetic structure model, and the value of the canted-layer thickness was deduced.
参考文献
| [1] | Birringer R;Herrand U;Gleiter H .[J].Suppl Trans Japan Inst Metals,1986,27(01):43. |
| [2] | Birringer R .[J].Physics Letters,1984,102A:524. |
| [3] | 黄波.固体材料及应用[M].广州:华南理工大学出版社,1995:182. |
| [4] | 陈德顺,丘其春,熊茂仁.混合烧结磁电复合材料的研究[J].华南理工大学学报（自然科学版）,1996(03):111. |
| [5] | H Tamura;E Matijevic .[J].Journal of Colloid and Interface Science,1988,26(01):62. |
| [6] | Fresnius w et al.[J].Journal of the American Ceramic Society,1988,71(01):26. |
| [7] | P Mollard;P Germi;A Rousset .[J].Physical Review B,1977,86-88:1393. |
| [8] | A H Morrish;K Haneda .[J].Journal of Magnetism and Magnetic Materials,1983,35:105. |
| [9] | P. Kishan et al.[J].Indian Journal of Pure and Applied Mathematics,1981,19:83. |
| [10] | K Haneda;A H Morrish .[J].Journal of Applied Physics,1988,63(08):4258. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%