乙炔在高频等离子体电弧中高温分解,连续批量合成炭黑烟炱.高分辨透射电镜(HRTEM)观察发现,炭黑粒子大小约为25nm,由无定形碳和结晶不完整的石墨碎片组成.采用紫外/可见吸收光谱(UV-Vis),付立叶变换红外光谱(FT-IR)等分析方法,对其甲苯提取液及结晶产物进行了初步的成份确认,发现其中含有C60/C70富勒烯成份,粗含量达到烟炱的3%左右.
参考文献
| [1] | Kratschmer W et al.Solid C60:a new form of carbon[J].Nature,1990,347:354. |
| [2] | Guillard T et al.Large scale fullerences synthysis solar reactor modelling and first experimental results[J].Proc Int Sym Thermal Concertating Technology(STCT-9),1999,3(03):59. |
| [3] | Howard et al.Fullerences synthesis in combustion[J].Carbon,1992,30(08):1183. |
| [4] | R 塔洛 .富勒烯的制备方法[P].CN:1131408,1998. |
| [5] | 乔桂文 .富勒烯族碳素材料的制备方法及其在电池电极材料中应用[P].CN:1188073,1998. |
| [6] | Jenkins et al.Continuous production of fullerences by pyrolysis of acetylene at a glasssy carbon surface[J].CARBON,1998(36):1725. |
| [7] | Bilodeau JF et al.Modeling of the sysnthesis of fullerences by the thermal plasma dissocication of C2C14[J].Proc Int Sym Plasma Chem(ISPC-13),1997,4(04):1618. |
| [8] | 郝润蓉.碳 无机化学丛书[M].北京:科学出版社,1998:21. |
| [9] | 秀君晖.炭黑表面性能的表征[J].炭素,1999(04):8-12. |
| [10] | 唐光诗.关于富勒烯形成机理的一种推测[J].北京化工大学学报（自然科学版）,1999(02):80-82. |
| [11] | Iordache etal .New methods to obtain C60 and higher fullerences[J].Fullerence Science and Technology,1999,7(01):111. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%