用电导率电池测量了钠铁磷熔体的电阻率,并分析了相应玻璃的穆斯堡尔谱,计算了铁离子的价态和氧化还原比,分析了温度、时间和氧化钠含量对熔体电阻率和玻璃氧化还原比的影响.发现在Na2O含量低的熔体中,升温和降温过程的电阻率的变化是不可逆的,随着Na2O含量增加,不可逆性消失,熔体的电阻率随时间轻微下降.同时发现Na2O含量低的铁磷熔体的导电机理是电子性的,并用氧化还原比解释了其电阻率-温度曲线的不可逆性.
参考文献
[1] | Chen Fuyi;D .Day An Irreversibility Phenomena in Electrical Conductivity of the Melts in Sodium Iron Phosphates System[J].金属学报(英文版),1999,12:324-328. |
[2] | R H Doremus.Electrical Conductivity and Ion Diffusion in Glass Sicence Second edition[M].a wiely-inter science publication,1994:263-290. |
[3] | N F Mott .Conduction in Glass Containing Transition Metal Ions[J].Journal of NON-CRYSTALLINE SOLIDS,1968,1:1-17. |
[4] | L Murawski .Electrical Conductivity in Iron-containing Oxides Glasses[J].Journal of Materials Science,1982,17:2155-2163. |
[5] | N F Mott;E A Davis.Electronic Processes in NonCrystalline Materials[M].Claredon Oxford,1979 |
[6] | Katsuhisa Tanaka;Toshinobu Yoko;Masahiro nakano .Electronic Conduction in Fe2O3-TeO2-P2O5[J].Journal of Non-Crystalline Solids,1990,125:264-271. |
[7] | A Mogus-Milankovic;Delbert E Day .Thermally Stimulated Polarization and DC Conduction in Iron Phosphate Glasses[J].Journal of Non-Crystalline Solids,1963,162:275-286. |
[8] | H Nasu;N Soga .Temperature Dependence of Electrical Conduction of the Sodium-iron Phosphate Glasses[J].Journal of Non-Crystalline Solids,1982,53:101-112. |
[9] | R E Tickle .The Electrical Conductance of Molten Alkali Silicate. Part 1. Experiments and Results[J].Physics and Chemistry of Glasses,1967,8(03):101-112. |
[10] | H Wakabayashi;R Terai .Measurement of Electrical Conductivity for Molten Glass[J].Journal of the Ceramic Society of Japan,1983,91(07):334-338. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%