由高硫焦制备出一系列超级活性炭,并在0～10MPa、93～293K范围内,考察了SBET为3886m2*g-1的超级活性炭对氢的吸附、解吸特性.结果表明,氢的吸附能力随超级活性炭比表面积的升高而增加,随着温度的降低而增大;在293K/5MPa、93K/6MPa条件下,储氢质量分数分别达1.9wt%、9.8wt%;氢的等温脱附率为95.9%.
参考文献
| [1] | 郑青榕,顾安忠.储氢技术的新进展[J].新能源,2000(12):120-127. |
| [2] | Si Hyun Lee;Cheong Song Choi .Chemical activation of high sulfur petroleum cokes by alkali metal compounds[J].Fuel Processing Technology,2000,64:141-153. |
| [3] | Carrasco-Marin;Miguel A;Alvarez-Merino et al.Microprous activated carbon from a bituminous coal[J].Fuel,1996,75(08):966-970. |
| [4] | 韩松,管正捷,古可隆,刘军利.石油焦制高比表面积粉状活性炭[J].石油化工,2000(03):171-175. |
| [5] | K A G mankwah;J S Noh;A Schwarz .Int.Hydrogen storage on superactivated carbon at refeigeration temperatures[J].Journal of Hydrogen Energy,1989,14(07):437-447. |
| [6] | J S Noh;R.K.Agarwal;A.Schwarz .Hydogen storage systems using activated carbon[J].International Journal of Hydrogen Energy,1987,12(10):693-700. |
| [7] | 周理.氢能利用与高表面活性炭吸附储氢技术[J].科技导报,1999(12):10-11. |
| [8] | 周理;周亚平 .关于氢在活性炭上高压吸附特性的实验研究[J].中国科学B辑,1996,26(05):473-479. |
| [9] | 况建华;许斌.超高表面积活性炭[J].炭素技术,1998(01):25-27. |
| [10] | Bradlef P Russell;M.Douglas Levan .Pore size distribution of BPL activated carbon determined by different methdos[J].CARBON,1994,32(03):845-855. |
| [11] | 杨骏兵,凌立成,刘朗.利用聚合物共混法对活性炭材料的孔径分布进行控制的原理和方法[J].材料导报,2000(04):48-50,29. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%