利用浸没法腐蚀实验研究了NiAl-28Cr-5 8Mo-0 2Hf和Ni-25Al-15Cr合金在750℃下,LiCl-10wt%Li2O熔盐中的腐蚀行为.实验结果表明:NiAl-28Cr-5 8Mo-0 2Hf和Ni-25Al-15Cr两种合金在750℃,LiCl-10wt%Li2O熔盐中的腐蚀产物都为LiCrO2、LiAlO2,NiAl-28Cr-5 8Mo-0 2Hf合金的耐蚀性能优于Ni-25Al-15Cr合金,主要是由于NiAl-28Cr-5 8Mo-0 2Hf合金两相里的NiAl(β)相的腐蚀滞后于Cr(Mo)相的腐蚀.在此种熔盐腐蚀环境下,两种合金形成的腐蚀层都是非保持性的,因此腐蚀动力学曲线呈直线.
参考文献
| [1] | S H Cho;J S Zhang et al.Corrosion behavior ofheat-resistant alloys of More 1 and Super 22H in molten salt of LiCl and LiCl-Li 2O[J].Korean Journal of Materials Research,1999,9(10):556. |
| [2] | S H Cho;J S Zhang et al.Corrosion behavior and effect of alloying element of Fe-based and Ni-based superalloys in motent salts of LiCl and LiCl-Li 2O[J].Korean Journal of Materials Research,1999,9(09):985. |
| [3] | S H Cho;J S Zhang et al.A study on the corrosion behavior austenitic stainless steel in hot molten salt of LiCl and LiCl-Li 2O[J].Korean Journal of Materials Research,1999,9(02):211. |
| [4] | S K Pabi;J Joardar et al.Nonocrystralline phases in Cu-Ni,Cu-Zn and Ni-Al systems by mechanical alloying[J].Nanostructured Materials,1996,9:149. |
| [5] | 夏东生;郭建亭 等.NiAl(Co)系机械合金化的研究[J].金属学报,1999,35(03):320. |
| [6] | K E Harris;F Ebrahimi et al.Texture evolution in NiAl[J].Material Science and Engineering,1998,A247:187. |
| [7] | 崔传勇;郭建亭 .NiAl-28Cr-5Mo-1Hf多相金属间化合物的显微组织及力学性能研究[J].金属学报,1999,35(05):477. |
| [8] | C.Y. Cui;Y.X. Chen;J.T. Guo .Preliminary investigation of directionally solidified NiAl-28Cr-5.5Mo-0.5Hf composite[J].Materials Letters,2000(5/6):303-308. |
| [9] | 陈玉喜;崔传勇 等.定向凝固NiAl-Cr(Mo)-Hf合金微观结构的电子显微学研究[J].金属学报,1999,35(09):897. |
| [10] | Ni-25Al-15Cr多相金属间化合物的显微组织[J].中国有色金属学报,1999(03):499. |
| [11] | 徐春梅,郭建亭,杨福宝.NiAl-28Cr-5Mo-1Hf合金的高温氧化行为研究[J].金属学报,2001(08):857-860. |
| [12] | R A Rapp;Y S Zhang.Hot Corrosion of Materials-Fundamental Aspects[J].Modern Salt Forum,1998:25. |
| [13] | 张永刚;韩雅芳.金属间化合物结构材料[M].北京:国防工业出版社,2001 |
| [14] | 朱日彰;何业东.高温腐蚀及耐高温腐蚀材料[M].上海:上海科学技术出版社,1993 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%