本文采用溶胶-凝胶法制备纳米二氧化钛和掺锆二氧化钛粉末.TGA表征分析发现掺锆后二氧化钛吸附水量增加.SEM和BET表征显示掺锆粒子半径减小,比表面积增加.XRD分析发现掺锆后的衍射峰宽化,晶粒变小,与SEM和BET结果吻合,还发现掺锆抑制了二氧化钛晶相转变.光催化降解亚甲基蓝结果表明,当锆掺杂浓度在5%,焙烧温度530℃时,掺锆二氧化钛催化活性最高.
参考文献
[1] | 张彭义;余刚;蒋展鹏 .半导体光催化剂及其改性技术进展[J].环境污染治理技术与设备,1997,5(03):2-10. |
[2] | 张俊平,陈萍.以十二烷基苯磺酸钠为模型反应物的Y2O3/TiO2复合催化剂的制备及光降解催化性能[J].感光科学与光化学,2002(04):241-246. |
[3] | 钱斯文,王智宇,王民权.La3+掺杂对纳米TiO2微观结构及光催化性能的影响[J].材料科学与工程学报,2003(01):48-52. |
[4] | Kim J;Song K C;Foncillas S;Pratsins S E .Dopants for synthesis of stable bimodally porous titania[J].Journal of the European Ceramic Society,2001,21(16):2863-2872. |
[5] | Yang J.;Ferreira JMF. .On the titania phase transition by zirconia additive in a sol-gel-derived powder[J].Materials Research Bulletin: An International Journal Reporting Research on Crystal Growth and Materials Preparation and Characterization,1998(3):389-394. |
[6] | ZHANG Y H;Xiong G X;Yao N et al.Prepartation of titania-based catalysts for formaldehyde photocatalytic oxidation from TiCl4 by the sol-gel method[J].Catalysis Today,2001,68(13):89-95. |
[7] | de Farias;Robson F;Airoldi C .Spherical Particles of Zirconia-Titania of Hexagonal Structure from a Neutral Amine Route[J].Journal of Colloid and Interface Science,1999,220(02):255-259. |
[8] | 刘守新,孙承林.光催化剂TiO2改性的研究进展[J].东北林业大学学报,2003(01):53-56. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%