众所周知表面接枝类聚乙二醇(PEG)可以改善材料的生物相容性.本文研究了氧/二(乙二醇)甲醚低温等离子体条件下NiTi合金表面接枝PEG结构及其性质.经X射线光电子能谱(XPS)、衰减全反射红外光谱(ATR-FTIR)、扫描电镜(SEM)和水接触角的分析和表征,证实沉积的涂层为类PEG结构,表面主要聚集大量(-CH2-CH2-O)n键;与改性前相比,接枝后的NiTi合金亲水性有较大提高.
参考文献
| [1] | 杨凯,辜承林.形状记忆合金的研究与应用[J].金属功能材料,2000(05):7-12. |
| [2] | Ryhanen J et al.[J].Journal of Biomedical Materials Research,1997,35(04):451. |
| [3] | 王昌祥;成治清 .[J].功能材料,1999,30(03):246. |
| [4] | Agnes R D;Eileen B S et al.[J].Journal of Applied Polymer Science,2001,81:3425-3438. |
| [5] | Lin Sichong.[J].Polymer Bulletin,1997(01):1-7. |
| [6] | Denes F.;Hua Z.Q.;Simonsick W.J.;Aaserud D.J. .Synthesis and Characterization of Teflon-Like Macromolecular Structures from Dodecafluorocyclohexane and Octadecafluorodecalin Under RF-Cold-Plasma[J].Journal of Applied Polymer Science,1999(10):1627-1639. |
| [7] | Tang L;Wu Y;Timmons RB .Fibrinogen adsorption and host tissue responses to plasma functionalized surfaces.[J].Journal of biomedical materials research, Part B. Applied biomaterials,1998(1):156-163. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%