本文研究了激光重熔等离子喷涂锌铝基Al2O3陶瓷复合层的组织结构.结果表明,等离子喷涂Al2O3陶瓷涂层主要由等轴晶状的α-Al2O3陶瓷相组成,长条状的γ-Al2O3陶瓷相量较少,主要分布在α-Al2O3陶瓷相的相界面和几个α-Al2O3陶瓷相晶粒的交汇处;激光重熔后基体相树枝晶得到明显细化,熔池区只存在单一的δ-Al2O3陶瓷相,原α-Al2O3陶瓷相、γ-Al2O3陶瓷相均转变为δ-Al2O3陶瓷相,陶瓷颗粒独立地分布于基体相中,表层陶瓷颗粒数目众多,并有局部富集现象,次表层次之,而在过渡区只能偶尔发现独立存在的陶瓷颗粒.
参考文献
| [1] | Yang Yuanzheng;Zhu Youlan;Liu Zhengyi;Chuang Yuzhi .Laser remelting of plasma sprayed Al{sub}2O{sub}3 ceramic coatings and subsequent wear resistance[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2000(1/2):168-172. |
| [2] | M F Zawrah and et al.[J].Materials Science and Engineering A,2002,332:167-173. |
| [3] | Guy Antou et al.[J].Surface and Coatings Technology,2003,172:279-290. |
| [4] | K H zum Gahr;J Schneider .[J].Ceramics International,2000,26:363-370. |
| [5] | Yanxiang Li;Jiankui Yao;Yuan Liu .[J].Surface and Coatings Technology,2003,17:57-64. |
| [6] | 周香林;于家洪;陈传忠.[J].金属热处理,1996(06):43-45. |
| [7] | 陈传忠;于慧群 等.[J].陶瓷学报,1998,19(01):12-16. |
| [8] | 杨元政,刘正义,庄育智.等离子喷涂Al2O3陶瓷涂层的结构与组织特征[J].兵器材料科学与工程,2000(03):7-11. |
| [9] | 斯松华,袁晓敏,何宜柱.激光熔覆等离子喷涂Al2O3陶瓷涂层组织结构研究[J].表面技术,2002(04):11-14. |
| [10] | 杨元政,刘志国,刘正义,庄育智.激光法在测量矩形截面三分支管湍流流场中的应用[J].激光杂志,2000(01):51-52. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%