研究了不锈钢粉末表面化学镀铜对烧结不锈钢组织和耐蚀性的影响.实验表明,以化学包覆不锈钢粉的形式加入1～5wt%的铜,在1150℃液相烧结时,在烧结不锈钢中,铜元素分布的均匀性以及烧结体的密度比机械混合方式加入铜都有很大提高;同时通过电化学实验表明,化学镀铜方式有利于提高不锈钢烧结体的耐蚀性.
参考文献
| [1] | D.Whittaker .[J].International Journal of Powder Metallurgy,1998,34(03):17-24. |
| [2] | 黄培云.粉末冶金原理[M].北京:冶金工业出版社,1988 |
| [3] | A Tiziani;A Molinari;L Fedrizzi et al.[J].Powder Metallurgy,1989,32(02):118-121. |
| [4] | RPMJones .[J].Progress in Powder Metallurgy,1974,26:258. |
| [5] | A Sharon;D Itzhak .[J].Materials Science and Engineering,1997,224:177-186. |
| [6] | A Tiziani;A Molinari;J Kazior et al.[J].Powder Metallurgy International,1990,22(04):17-19. |
| [7] | R M German.Liquid Phase Sintering[M].PlenumPress,NewYork,1985:22. |
| [8] | 郭庚辰 .[J].粉末冶金工业,1998,8(04):30-37. |
| [9] | F Deflorian;L Ciaghi;J Kazior .[J].Werkstoffe und Korrosion,1992,43(09):447-452. |
| [10] | A Sharon;D Itzhak .[J].Materials Science and Engineering,1997,224:177-186. |
| [11] | H.H.Uhlig.[M].Corrosion and Corrosion Control,1971:69. |
| [12] | D.Itzhak;P. Peled .[J].Corrosion Science,1986,26(01):49-54. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%