研究了环境气氛、动态渗氢及预渗氢对不同有序度Ni2Cr合金脆化的影响.结果表明,有序度对Ni2Cr合金在室温空气及氢气中的环境氢脆没有明显影响;动态渗氢拉伸时Ni2Cr合金存在严重的氢脆敏感性,无序和高度有序合金比部分有序合金脆化严重;预渗氢时,氢原子通过晶格扩散及晶界扩散进入合金,Ni2Cr合金氢脆敏感性随有序度的增大而减小.
参考文献
| [1] | G M Camus;N S Stoloff;D J Duqutte .[J].Acta Materialia,1989,37:1497-1501. |
| [2] | C Nishimura;C T Liu .[J].Scripta Metallurgica et Materialia,1996,35:1441-1447. |
| [3] | X Y Cheng;X J Wan .[J].Scripta Metallurgica et Materialia,2001,44:325-329. |
| [4] | J erkowitz;C Miller .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1980,11:1877-1881. |
| [5] | J erkowitz;M Kurkela;R M Latanision.[J].Metallurgical Soc of AIME,1981:411-418. |
| [6] | K Miyata;M Igarashi .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1992,23:953-961. |
| [7] | J K Tien;A W Thompson;I M Bernstein et al.[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1976,7:821-829. |
| [8] | 张德志;邹明达;肖纪美 .[J].材料科学与工程,1997,15:15-17. |
| [9] | X Y Cheng;X J Wan .[J].Scripta Metallurgica et Materialia,2002,46:465-470. |
| [10] | 姚美意 .Co基、Ni基、Fe基、Ti基金属间化合物在H2中脆化的研究[D].上海:上海大学,1999. |
| [11] | 李慧改 .有序度对Ni<,2>Cr合金氢致脆断的影响[D].上海大学,2004. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%