采用X射线、光学显微镜、扫描电镜及透射电镜等手段研究了微量稀土Y对2519合金的显微组织及耐热性能的影响.结果表明,在2519合金中Y元素与Cu,Al元素主要形成Al6Cu6Y金属间化合物,并沿晶界分布.这些金属间化合物有效阻碍高温时基体的变形和晶界的移动,提高合金高温强度.添加0.20%Y(质量分数)可使合金200℃时的抗拉强度提高30%,但伸长率有所下降.Y含量的进一步增加,含Y化合物聚集长大成块,合金室温及高温力学性能降低.同时发现,微量的Y细化了合金的再结晶组织,细化了合金强化相θ′相.添加0.10%Y时可使合金的室温强度提高20MPa.
参考文献
| [1] | B. Carter Hamilton;Ashok Saxena .Transient crack growth behavior in aluminum alloys C415-T8 and 2519-T87[J].Engineering Fracture Mechanics,1999(1):1-22. |
| [2] | L.S. Kramer;T.P. Blair;S.D. Blough .Stress-Corrosion Cracking Susceptibility of Various Product Forms of Aluminum Alloy 2519[J].Journal of Materials Engineering and Performance,2002(6):645-650. |
| [3] | Dymek S.;Dollar M. .TEM investigation of age-hardenable Al 2519 alloy subjected to stress corrosion cracking tests[J].Materials Chemistry and Physics,2003(2/3):286-288. |
| [4] | James J. Fisher Jr.;Lawrence S. Kramer;Joseph R. Pickens .ALUMINUM ALLOY 2519 IN MILITARY VEHICLES[J].Advanced Materials & Processes,2002(9):43-46. |
| [5] | 王祝堂;田荣章.铝合金及加工手册[M].长沙:中南工业大学出版社,1988:172. |
| [6] | 王庆良,王大庆.稀土钇对AlZnMgCu合金组织及性能的影响[J].中国矿业大学,1999(04):382-385. |
| [7] | 王建华,易丹青,卢斌,刘沙,曹昱.钇对2618合金组织及性能的影响[J].中国稀土学报,2002(02):150-153. |
| [8] | 肖程波,韩雅芳.硫和钇在含钇Ni3Al基IC6合金高温氧化过程中的界面行为[J].中国稀土学报,1999(04):377-380. |
| [9] | 肖代红,王健农,陈世朴,丁冬雁.铈对高Cu/Mg比率Al-Cu-Mg合金组织和耐热性能的影响[J].中国稀土学报,2003(05):564-567. |
| [10] | 曾令民,郑建宣.钇对Al-Cu-Mg三元系α相区及硬铝性能的影响[J].中国稀土学报,1989(04):77. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%