在20℃长期养护条件下,当碱含量为2.5%时,掺加Li/Na摩尔比0.6的LiF能长期有效抑制碱集料反应嘭胀.研究发现:集料活性越高,LiF对膨胀抑制效果越好.对于沸石化珍珠岩砂浆,在有效抑制碱集料反应膨胀的前提下,随着Li/Na摩尔比进一步的增加,LiF对碱集料反应膨胀的抑制效果并没有得到相应的提高.此外,掺加LiF一定程度上降低了砂浆的抗压强度和抗折强度,掺量越大,强度降低越多.在相同碱含量条件下,掺加LiF能缩短水泥的凝结时间,且Li/Na摩尔比越大,凝结时间越短.
参考文献
| [1] | 莫祥银,许仲梓,唐明述.国内外混凝土碱集料反应研究综述[J].材料科学与工程,2002(01):128-132. |
| [2] | StarkD;Morgan B;Okamoto P.Eliminating or minimizing alkali-silica reactivity Strategic Highway Research Program[J].Washington D C:National Research Council,1993 |
| [3] | WangH;Tysl S;Gillot J E.Practical implications of lithium -based chemicals and admixtures in controlling alkali-aggregate reactions[M].SP148-20 Proc 4th Inter Conf On Superplasticizers and Chemical Admixtures in Concrete edited by Malhotra V M,1994:353-366. |
| [4] | Stokes D B;Manissero C E;Roy D M.Portland cement manufacture containing lithium for ASR control[A].,2000:773-781. |
| [5] | Baxter S Z;Stokes D B;Manissero C E.A lithium-based pozzolan for ASR control[A].,2000:573-582. |
| [6] | axterSZ .Glass formula for avoiding ASR[P].U: S: Patent 5803960,1998. |
| [7] | Whitmore David;Abbott S.Use of an applied electric field to drive lithium ions into alkali-silica reactive structures[A].,2000:1089-1098. |
| [8] | Johnston D P;Surdahl R;Stokes D B.A case study of a thiumbased treatment of an ASR-affected pavement[A].,2000:1149-1158. |
| [9] | Xiangyin Mo;Chenjie Yu;Zhongzi Xu .Long-term effectiveness and mechanism of LiOH in inhibiting alkali-silica reaction[J].Cement and Concrete Research,2003(1):115-119. |
| [10] | 莫祥银,李钢,王侠,许仲梓,吴科如.LiOH抑制碱集料反应长期有效性及机理的研究[J].硅酸盐学报,2003(02):118-121. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%