应用DC(直流)反应磁控溅射设备在硅基底上制备TiO2薄膜,在固定的电源功率下,氩气流量为42.6sccm,氧流量为15sccm,溅射时间为30分钟的条件下,通过控制温度改变TiO2薄膜的光学性质.应用n&k Analyzer 1200测量,当温度增加时薄膜的平均反射率降低同时反射低谷向长波方向移动；温度对消光系数k影响不大；当温度低于180℃薄膜的折射率变化不大,当温度达到240℃左右时薄膜的折射率明显降低.通过XRD和SEM表征发现,随着温度的增加TiO2的晶体结构由混晶变为单一的锐钛矿相,薄膜表面的颗粒由多变少,表面形貌由粗糙多孔变得细腻平滑.
参考文献
| [1] | Y -M Gao;H -S Shen;K Dwight;A Wold .[J].Materials Research Bulletin,1992,27:1023. |
| [2] | B O' Regan;M Gratzel .[J].Nature,1991,353:737. |
| [3] | A Hagfeldt;N Vlachopoulos;M Gratzel .[J].Journal of the Electrochemical Society,1994,141:L82. |
| [4] | A Hugot-Le;Goff P Falaras;J Electrochem .[J].Soc,1995,142:L38. |
| [5] | A Hagfeldt;M Gratzel .[J].Chemical Reviews,1995,95:49. |
| [6] | H K Pulker.Thin Film Science and Technology[J].Elsevier Amsterdam,1984 |
| [7] | A Fujishima;T Rao;D Tryk;J Photochem .[J].Journal of Photochemistry and Photobiology C:Photochemistry Reviews,1:1. |
| [8] | NADEL S.Proc. 39th Annual Technical Conf. of Society of Vacuum Coaters[C].,1996:157. |
| [9] | Marius D;Stamate U .[J].Thin Solid Films,372:246-249. |
| [10] | 郭兴龙,于先进,薛成山,董志华,高海永.磁控溅射制作金红石--TiO2[J].微纳电子技术,2003(12):20-21,42. |
| [11] | 张利伟,鲁占灵,杨仕娥,姚宁,张兵临.直流反应磁控溅射制备锐钛矿型TiO2薄膜[J].真空与低温,2003(04):221-223. |
| [12] | A R Forouhi;I Bloomer .[J].Physical Review B,1986,34:7018. |
| [13] | A R Forouhi;I Bloomer .[J].Physical Review B,1988,38:1865. |
| [14] | A R Forouhi;I Bloomer .[P].US 4,905,170 |
| [15] | J Rodriguez;M Gomez;J Ederth .[J].Thin Solid Films,2000,365:119-125. |
| [16] | 杨文华,李红波,吴鼎祥.太阳电池减反射膜设计与分析[J].上海大学学报(自然科学版),2004(01):39-42. |
| [17] | 唐伟忠.薄膜材料制备原理、技术及应用[M].北京:冶金工业出版社,1998:116. |
| [18] | Okimura K. .Low temperature growth of rutile TiO2 films in modified rf magnetron sputtering[J].Surface & Coatings Technology,2001(2/3):286-290. |
| [19] | 薛增泉.薄膜物理[M].北京:电子工业出版社,1991:55. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%