材料科学与工程学报, 2005, 23(3): 466-472. doi: 10.3969/j.issn.1673-2812.2005.03.039

复合材料层合板冲击损伤及剩余强度研究进展

崔海坡 1, , 温卫东 2, , 崔海涛 3,

1.南京航空航天大学能源与动力学院,江苏,南京,210016

2.南京航空航天大学能源与动力学院,江苏,南京,210016

3.南京航空航天大学能源与动力学院,江苏,南京,210016

关键词： 低速冲击 , 复合材料层合板 , 剩余强度 , 损伤

Advances of Study on Low Velocity Impact Damaged and Residual Strength of Composite Laminates

综述了受低速冲击后复合材料层合板的损伤研究进展,重点介绍了倍受复合材料工程结构设计师所关注的含损复合材料层合板的剩余拉伸及压缩强度问题,最后对有待于进一步研究的问题进行了展望.

参考文献

[1] 杨光松.损伤力学与复合材料损伤[M].北京:国防工业出版社,1995
[2] Choi HY;Wu HY;Chang FK .A new approach toward understanding damage mechanisms and mechanics of laminated composites due to low-velocity impact. Part Ⅱ. Analysis[J].Journal of Composite Materials,1991,25:1012-38.
[3] 沈真.含缺陷复合材料层压板的压缩破坏机理[J].航空学报,1991(03):105.
[4] Scarponi C.;Barboni R.;Marcone A.;Iannone M.;Briotti G. .IMPACT TESTING ON COMPOSITES LAMINATES AND SANDWICH PANELS[J].Journal of Composite Materials,1996(17):1873-1911.
[5] 程小全,张子龙,吴学仁.小尺寸试件层合板低速冲击后的剩余压缩强度[J].复合材料学报,2002(06):8-12.
[6] M.F.S.F. de Moura;A.T. Marques .Prediction of low velocity impact damage in carbon-epoxy laminates[J].Composites, Part A. Applied science and manufacturing,2002(3):361-368.
[7] Sun CT;Grady JE .Dynamic delamination fracture toughness of a graphite/exopy laminate under impact[J].Composites Science and Technology,1988,31:55-72.
[8] Choi HY;Wu HY;Chang FK .Effect of laminate configuration and impactor' s mass on the initial impact damage of graphite/epoxy composite plates due to line-loading impact[J].Journal of Composite Materials,1992,26:804-27.
[9] Olsson R.Impact response of composite laminates-a guide to closed form solutions, FFA TN, 1992-33[M].Bromma: The Aeron Res Inst of Sweden,1993
[10] Lakshminarayana HV;Boukhili R;Gauvin R .Impact response of laminated composite plates:prediction and verification[J].Computers and Structures,1994,28:61-72.
[11] ZhengS;Sun CT .A double-plate finite-element model for the impact-induced delamination problem[J].Composites Science and Technology,1995,53:111-8.
[12] B. Qi;I. Herszberg .An engineering approach for predicting residual strength of carbon/ epoxy laminates after impact and hygrothermal cycling[J].Composite Structures,1999(1/4):483-490.
[13] Choi HY;Chang FK .A Model for Predicting Damage in Graphite/Epoxy Laminated Composites Resulting from Low-Velocity Point Impact[J].Journal of Composite Materials,1992,26:2134-69.
[14] Lammerant L;Verpoest I .Modelling of the interaction between matrix cracks and delaminations during impact of composite plates[J].Composites Science and Technology,1996,56:1171-8.
[15] Luo RK;Green ER;Morrison CJ .Impact damage analysis of composite plates[J].International Journal of Impact Engineering,1999,22:435-47.
[16] Robin Olsson .Analytical prediction of large mass impact damage in composite laminates[J].Composites, Part A. Applied science and manufacturing,2001(9):1207-1215.
[17] J.P.Hou;N.Petrinic;C.Ruiz;S.R.Hallett .Prediction of Impact Damage in Composite Plates[J].Composites science and technology,2000(2):273-281.
[18] Chang F;Chang K .A progressive damage model for laminated composites containing stress concentrations[J].Journal of Composite Materials,1987,21:834-55.
[19] ASTM STP 568.Residual Strength Characterization of Laminated Composites Subjected to Impact Loading[S].Ametican society for Testing and Materials,Philadelphia,1975.
[20] Caprino G .Residual Strength Prediction of Impacted CFRP Laminates[J].Journal of Composite Materials,1984,18:508-518.
[21] Caprino G;Lopresto V .The significance of indentation in the inspection of carbon fibre-reinforced plastic panels damaged by lowvelocity impact[J].Composites Science and Technology,2000,60:1003-12.
[22] 施平 .受低速冲击后玻璃/环氧层板刚度与强度的关[J].哈尔滨工业大学学报,1992,24(04)
[23] 施平;阎相桥 .复合材料层板受低速冲击后的剩余刚度与剩余强度研究[J].宇航学报,1996,17(01):91-94.
[24] Charles E Harris .A progressive damage model and analysis methodology for predicting the residual strength of composite laminates[J].Journal of Composites Technology and Research,1997,19(01):3-9.
[25] Poe C C;w Illg;D P Garber .A program to determine the effect of low-velocity impacts on the strength of the filament-wound rocket motor case for the space shuttle[Z].NASA Technical Memorandum 87588,1985.
[26] Sarma Avva V;Padmanabha H L.Compressive Residual Strength Prediction in fiber-Reinforced Laminated Composites Subjected to Impact Loads[M].Advances in Fracture Mechanics, ICF,1984
[27] Cairns D S .Impact and Post-Impact Response of Graphite/Epoxy and Kevlar/Epoxy Structures[D].Ph.D.dissertation.Massachusetts Institute of Technology,1987.
[28] El-zein M S;Reifsnider K L .On the Prediction of Tensile Strength after Impact of Composite Laminates[J].Journal of Composites Technology and Research,1990,12(03):147-154.
[29] Tan S C .A progressive failure model for composite laminates containing openings[J].Journal of Composite Materials,1991,25:556-577.
[30] Harris C E .A progressive damage model and analysis methodology for predicting the residual strength of composite laminates[J].Journal of Composites Technology and Research,1997,19:3-9.
[31] Z Tian;S R Swanson .The Fracture Behavior of Carbon/Epoxy Laminates Containing Internal Cut Fibers[J].Journal of Composite Materials,1991,25:1427-44.
[32] Z Tian;S R Swanson .Residual tensile Strength predication on a ply-ply-ply basis for laminates containing impact damage[J].Journal of Composite Materials,1992,26(08):1193-1206.
[33] Poe C C .A Unifying Strain Criterion for Fracture of Fibrous Composite Laminates[J].Engineering Fracture Mechanics,1983,17:153-171.
[34] Nguyen BN. .THREE-DIMENSIONAL MODELING OF DAMAGE IN LAMINATED COMPOSITES CONTAINING A CENTRAL HOLE[J].Journal of Composite Materials,1997(17):1672-1693.
[35] 唐啸东,杨旭,陈业标.带损伤复合材料层压板剩余强度估算方法研究[J].航空学报,1997(02):146.
[36] G C Papanicolaou;Chr D Sravropoulos .New Approach for Residual Compressive Strength Prediction of Impacted CFRP Laminates[J].Composites,1995,26:517-523.
[37] Hosur MV;Murthy CRL;Ramurthy TS .Compression after impact testing of carbon fibre reinforced plastic laminates[J].Journal of Composites Technology and Research,1999,21:51-64.
[38] Recker et al.Toughened thermosets for damage tolerant carbon fiber reinforced composites[J].Sampe Journal,1990,26:73-78.
[39] Gottesman et al.Residual Strength of Impacted Composites: Analysis and Tests[J].Journal of Composites Technology and Research,1994,16:244-255.
[40] Girshovich.Impact Damage Assessment of Composite. in Damage Detection in Composite Materials[A].,1992:183-199.
[41] Soutis C;P T Curtis .Prediction of the Post-Impact Compressive Strength of CFRP Laminated Composites[J].Composites Science and Technology,1996,56:677-684.
[42] Soutis C N A Fleck;P A Smith .Failure Prediction Technique for Compression Loaded Carbon Fibre-Epoxy Laminate with a Single Hole[J].Journal of Composite Materials,1991,25:1476-98.
[43] Chang FK;Lessard LB .Damage Tolerance of laminated composites containing an open hole and subjected to compressive loadings:Part I - Analysis[J].Journal of Composite Materials,1991,25:2-43.
[44] Zafer Kutlu .Modeling Compression Failure of Laminated Composites Containing Multiple Through-the-Width Delaminations[J].Journal of Composite Materials,1992,26:350-387.
[45] Y. Xiong;C. Poon;P. V. Straznicky;H. Vietinghoff .A prediction method for the compressive strength of impact damaged composite laminates[J].Composite Structures,1995(4):357-367.
[46] 程小全,寇长河,郦正能.低速冲击后复合材料层合板的压缩破坏行为[J].复合材料学报,2001(01):115-119.
[47] 张子龙,程小全,益小苏.复合材料冲击损伤及冲击后压缩强度的等效实验方法[J].实验力学,2001(03):313-319.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
作者相关
文章评分
  • 您的评分：
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%

版权所有©2010中国科学院金属研究所中国科技出版传媒股份有限公司

本系统由北京仁和汇智信息技术有限公司设计开发

技术支持：info@rhhz.net