研究了不同组成的复合胶凝材料硬化浆体(硅酸盐水泥,硅酸盐水泥+粉煤灰,硅酸盐水泥+矿渣,硅酸盐水泥+硅灰,硅酸盐水泥+硅灰+粉煤灰)早龄期时裂纹扩展阻力的发展,探讨了粉煤灰掺量对裂纹扩展阻力的影响.结果表明:早龄期时,在相同水胶比条件下,掺加硅灰使胶凝材料体系裂纹扩展阻力明显降低,在低水胶比条件下,掺加一定量的粉煤灰能够明显增加体系的裂纹扩展阻力,掺加20%的粉煤灰能使胶凝材料具有较高的裂纹扩展阻力.
参考文献
| [1] | R Springenschmid.Prevention of thermal cracking in concrete at early ages[M].London: E&FN Spon,1998:1-5. |
| [2] | R W Burrows.The Visible and Invisible Cracking of Concrete[J].Monograph of ACI,1998 |
| [3] | P Kraai.A Proposed Test to Determine the Cracking Potential due to Drying Shrinkage of Concrete[J].Concrete Construction,1985:775-778. |
| [4] | R Springenschmid;E Gierlinger;W Kiemozycki.Thermal stresses in mass concrete: A new testing method and the influence of different cements[A].:57-72. |
| [5] | Surendra P Shah;Chengsheng Quyang et al.A method to predict shrinkage cracking of concrete[J].ACI Materials Journal,1998,95(04):339-346. |
| [6] | Chengsheng Ouyang;Surendra P .shah Geometry-Dependent R-curve for quasi-brittle Materials[J].Journal of the American Ceramic Society,1991,74(11):2831-2836. |
| [7] | D E McCabe.Fracture Toughness Evaluation by R-Curve Method[M].American Society for Testing and Materials.Philadelphia, PA,1973 |
| [8] | 赵国藩;彭少民;黄承逵.钢纤维混凝土结构[M].北京:中国建筑工业出版社,1999:84-89. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%