采用超声均相沉淀法,以硫代乙酰胺和硫酸亚铁铵为原料,通过调整溶液pH值,并借助表面活性剂防止颗粒团聚,在常温下合成了均匀分散的FeS纳米颗粒.X射线衍射和透射电镜(TEM)分析表明颗粒直径为40～50nm.将制备的FeS溶液涂在陶瓷板上进行化学气相沉积,得到了大量直径为5～8μm的气相生长碳纤维.
参考文献
| [1] | T. Hashishin;H. Iwanaga;M. Ichihara;S.R. Mukai .Core structure of vapor grown carbon fibers and morphology dependence of tensile strength[J].Carbon: An International Journal Sponsored by the American Carbon Society,2003(2):343-349. |
| [2] | G G Tibbetts;C P Beetz Jr .Mechanical properties ofvapour-grown carbon fibers[J].Journal of Applied Physics,1987,20:292-297. |
| [3] | G G Tibbetts;M Endo;C P Beetz Jr.Carbon fibers grown from the vapor Phase: a novel material[J].Sampe Journal,1986:30-35. |
| [4] | G G Tibbetts;Micheal P .Balogh. Increase in yield of carbon fibers grown above the iron/carbon eutectic[J].Carbon,1999,37:241-247. |
| [5] | A. Hoque;M. K. Alam;G. G. Tibbetts .Synthesis of catalyst particles in a vapor grown carbon fiber reactor[J].Chemical Engineering Science,2001(14):4233-4243. |
| [6] | 唐勇纯,苏堤,邓意达.均匀沉淀法制备ZnS超细粉的新方法[J].贵州化工,2003(02):27-29. |
| [7] | 杨富国,朱琼霞,方正.快速均匀沉淀法制备纳米微粒ZnS[J].中南工业大学学报(自然科学版),2001(03):270-272. |
| [8] | N G Harmandas;P G Koutsoukos .The formation of iron (Ⅱ)sulfides in aqueous solutions[J].Cryst Growth,1996,167:719-724. |
| [9] | 陈凡,励亮,孙晓宇,乐英红,胡建华.均相沉淀法制备纳米硫化亚铁[J].复旦学报(自然科学版),2003(03):315-318. |
| [10] | 李春喜,王子镐.超声技术在纳米材料制备中的应用[J].化学通报,2001(05):268-271,267. |
| [11] | 华东化工学院分析化学教研组.分析化学[M].北京:高等教育出版社,1989:152-194. |
| [12] | 成会明.纳米碳管制备、结构、物性及应用[M].北京:化学工业出版社,2002:48-52. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%