利用维氏硬度仪和X射线应力分析仪、X射线衍射仪等手段分别对单层和层状氧化锆陶瓷进行了力学性能测试和分析,研究结果表明,在ZrO2层状复合陶瓷中,压痕裂纹的形成除了因塑性区体积变化产生的残余应力外,还与相变应力和表面压应力有关,表面压应力对表面裂纹具有较大的抑制作用.层状陶瓷断裂韧性提高,主要是通过表面压应力对压痕裂纹区应力强度因子的贡献、提高断裂相变量,强化相变增韧效果、细化晶粒等几个方面来实现的.
参考文献
| [1] | 陈蓓,丁培道,周泽华.Al2O3/ZrO2层状复合陶瓷的结构设计与性能[J].硅酸盐学报,2001(04):386-388. |
| [2] | LawnB R;Evans A.G;Marshall D B .[J].Journal of the American Ceramic Society,1984,63(9-10):574. |
| [3] | Evans A G;Heuer AH .Review: Transformation toughening in ceramic-martensitic transformation in crack-tip stress field[J].Journal of the American Ceramic Society,1984,63(5-6):314. |
| [4] | Marshall D B;Lawn B R .Residual stress effects in sharp contact cracking:Indentation fracture mechanics[J].Journal of Materials Science,1979,14(08):2001-12. |
| [5] | 包亦望,苏盛彪,黄肇瑞.对称型陶瓷层状复合材料中的残余应力分析[J].材料研究学报,2002(05):449-457. |
| [6] | RALPH F K Jr .Estimation of characteristic parameters of a grain bridging model for crack extension[J].Journal of the American Ceramic Society,1999,82:373-375. |
| [7] | 陈蓓,丁培道,程川.Al2O3/ZrO2层状复合陶瓷的显微结构特征与强韧化的关系[J].材料导报,2004(09):92-93,98. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%