应变控制比例及非比例载荷低周疲劳试验结果表明,非比例载荷下钛合金BT9附加强化程度很小,而疲劳寿命降低明显.采用透射电镜(TEM)对钛合金BT9的疲劳位错亚结构进行了观测和分析,结果表明,钛合金BT9比例、非比例载荷下出现的多滑移位错亚结构都呈条块状;位错密度随等效应变强度、相位角的增加而增加,且分布极不均匀;非比例载荷下钛合金BT9中的局部高密度位错是其低周疲劳损伤程度加剧及寿命降低的主要因素.
参考文献
| [1] | H F Huang;S L Liu .Crack growth behaveior in Titianium alloy TC11 at room and high temperatures[J].Acta Metallurgica Sinica,1999,12(01):77-81. |
| [2] | Sun Xinjun,Bai Bingzhe,Gu Jialin,Chen Nanping.Mechanical Behaviors and Microstructural Characteristics of TC11 Alloy during Hot Deformation[J].稀有金属（英文版）,2000(02):101-109. |
| [3] | 海杰;王洪顺;赵艳君 等.α、β相分布形态对TC11钛合金高温低周疲劳寿命的影响[J].沈阳航空工业学院学报,2000,17(03):5-8. |
| [4] | W. D. Zeng;Y. G. Zhou .The influence of microstructure on dwell sensitive fatigue in Ti-6.5Al-3.5Mo-1.5Zr-0.3Si alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2000(1/2):33-38. |
| [5] | 于海生.疲劳失效准则在钛合金BT9低周 疲劳寿命估算中的应用[J].机械科学与技术,2001(01):66-68. |
| [6] | Doong S H;Socie D F;Robertson I M .Dislocation substructure and nonproportional hardening[J].ASME Journal of Engineering Materials and Technology,1990,112(04):456-464. |
| [7] | 肖林,白菊丽.Zr-4合金双轴疲劳行为及其微观变形机理Ⅱ.双轴循环变形亚结构及其织构的发展[J].金属学报,2000(09):919-925. |
| [8] | X.FEAUGAS;PH.PILVIN;M.CLAVEL .CYCLIC DEFORMATION BEHAVIOUR OF AN α/β TITANIUM ALLOY-II. INTERNAL STRESSES AND MICROMECHANIC MODELLING[J].Acta materialia,1997(7):2703-2714. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%