采用不同形貌的羟基磷灰石纳米粒子与聚酸酐材料复合,研究了羟基磷灰石形貌对复合材料力学强度的影响,并用扫描电子显微镜观察了复合材料的断面形态.结果发现羟基磷灰石的形貌对材料的压缩强度和压缩弹性模量影响较大:长针状羟基磷灰石增强效果较好,所得复合材料的压缩强度可达256MPa,压缩弹性模量可达9.8GPa;片状羟基磷灰石的复合材料力学强度较差,压缩强度最高只有160Mpa,压缩弹性模量最高只有7.9GPa.
参考文献
| [1] | 李世普.生物医用材料导论[M].武昌:武汉工业大学出版社,2000 |
| [2] | Bonfield W;Grynpas M D;Tully A E .Hydroapatite reinforced polyethylene a mechanically compatible implant material for bone replacement[J].BIOMATERIALS,1981,2:185-186. |
| [3] | Wang M;Bonfield W;Hench L L .Bioglasss / high density polyethylene composite as a new soft tissue bonding material[J].Bioceramics,1995,8:383-388. |
| [4] | M. S. Abu Bakar;P. Cheang;K. A. Khor .Thermal processing of hydroxyapatite reinforced polyetheretherketone composites[J].Journal of Materials Processing Technology,1999(0):462-466. |
| [5] | 张翔,李玉宝,宋之敏,左奕,吕国玉,牟元华.PA66/HA复合生物材料的力学性能研究[J].中国塑料,2005(06):25-29. |
| [6] | Gao W M;Li Q Y;Chen Y F .The effect of amino acids on synthesis of hydroxyapatite nanoparticles by hydrothermal treating[J].Key Engineering Materials,2005,280-283:1533-1536. |
| [7] | Anseth K S;Wang C M;Bowman C N .Reaction behavior and kinetic constant for photopolymerizations of multi (meth)acrylate monomers[J].Polymer,1994,35:3243-3250. |
| [8] | 杨志明.从临床观点探讨人工骨材料研究[J].材料导报,2000(03):6-8. |
| [9] | 张锦;张乃恭.新型复合材料力学机理及其应用[M].北京:北京航空航天大学出版社,1993 |
| [10] | 王学江,李玉宝.羟基磷灰石纳米针晶与聚酰胺仿生复合生物材料研究[J].高技术通讯,2001(05):1-5. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%