采用溶胶-凝胶旋转包覆法在玻璃衬底上制备了CO0.8Fe2.2O4薄膜.用振动样品磁强计和X射线衍射仪对样品的磁性和结构进行了室温及高温原位测量;用X射线光电子能谱仪和原子力显微镜测量了样品的成分及表面形貌.室温测量结果表明,400%退火时,样品已生成单一的尖晶石相,随退火温度升高衍射峰增高.样品的晶粒尺寸较小(14.2～29.6 nm),有利于降低磁记录材料的晶界噪音.630%退火样品的矫顽力达到1.56 X 105A·m-1.高温原位测量发现,500%高温时线膨胀系数约为1.3 X 10-5K-1,显示样品结构的热稳定性非常好,适合于磁光记录过程.随温度升高,样品由亚铁磁性逐渐过渡到顺磁性.
参考文献
| [1] | B. H. Liu;J. Ding .Strain-induced high coercivity in CoFe_(2)O_(4) powders[J].Applied physics letters,2006(4):042506-1-042506-3-0. |
| [2] | B X Gu .Magnetic properties and magneto-optical properties of Co0.5Fe2.5O4 nanestructured film[J].Applied Physics Letters,2003,82:3707-3709. |
| [3] | Biao Zhou;Ya-Wen Zhang;Yue-Jun Yu;Chun-Sheng Liao,ChunHua Yan .Correlation between structure and intervalence chargetgansfer transitions in nanocrystalline CoFe2-xMxO4(M=Mn,Al,Sc)thin films[J].Physical Review B:Condensed Matter,2003,68(1-8):024426. |
| [4] | 车仁超;李永清;陈朝辉;程海峰 林红吉 杨孚标 .钴铁氧体微粉的化学制备工艺及磁特性研究[J].功能材料,1999,30(06):615-616. |
| [5] | 焦永芳,李锐,刘钧,方庆清.Co2+对CoxFe3-xO4铁氧体结构与磁特性的影响[J].功能材料与器件学报,2005(04):481-484. |
| [6] | 汪金芝,方庆清.纳米Zn0.6CoxFe2.4-xO4晶粒的结构相变与磁性研究[J].物理学报,2004(09):3186-3190. |
| [7] | Cheng FX.;Liao CS.;Xu ZG.;Gao S.;Yan CH.;Wang DJ.;Wang J.;Peng ZY. .Chemical synthesis and magnetic study of nanocrystalline thin films of cobalt spinel ferrites[J].Solid State Communications,1998(9):471-476. |
| [8] | 刘世宏;王当憨;潘承璜.X射线光电子能谱分析[M].北京:科学出版社,1988:315-318. |
| [9] | Lance Horng;G. Chern;M. C. Chen .Magnetic anisotropic properties in Fe_3O_4 and CoFe_2O_4 ferrite epitaxy thin films[J].Journal of Magnetism and Magnetic Materials,2004(3):389-396. |
| [10] | 宛德福;马兴隆.磁性物理学[M].成都:电子科技大学出版社,1994:377. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%