采用无接触电阻测量方法,通过电阻率随水化时间的关系曲线,研究了粉煤灰水泥中加入NaOH和Na2SO4后净浆水化早期电阻率的变化规律.结果显示,加入粉煤灰后,使早期电阻率明显增加,后期电阻率降低.加入碱后,水化初期电阻率减低,后期电阻率增加.通过不同水化时间电阻率的变化曲线可以研究粉煤灰的持碱效应,并研究碱在粉煤灰水泥中的作用和形成的产物.
参考文献
[1] | 王培铭;陈志源;Scholz H .粉煤灰与水泥浆体间界面的形貌特征[J].硅酸盐学报,1997,25(04):475-479. |
[2] | Etsuo Sakai;Shigeyoshi Miyahara;Shigenari Ohsawa .Hydration of fly ash cement[J].Cement and Concrete Research,2005(6):1135-1140. |
[3] | Shiqun Li;Della M Roy;Amitabha Kumar .Quantitative determination of pozzolanas in hydrated systems of cement or Ca(OH)2 with fly ash or silica fume[J].Cement and Concrete Research,1985,15:1079-1086. |
[4] | Weiping Ma;Chunling Liu;Paul W Brown et al.Pore structures of fly ashes activated by Ca(OH)2 and CaSO4·2H2O[J].Cement and Concrete Research,1995,25(02):417-425. |
[5] | S Ohsawa;K Asaga;S Goto et al.Quantitative determination of fly ash in the hydrated fly ash-CaSO4·2H2O-Ca(OH)2 system[J].Cement and Concrete Research,1985,15:357-366. |
[6] | Michael Grutzeck;Stephen Kwan;Maria DiCola .Zeolite formation in alkali-activated cementitious systems[J].Cement and Concrete Research,2004(6):949-955. |
[7] | A. Fernandez-Jimenez;A. Palomo;M. Criado .Microstructure development of alkali-activated fly ash cement: a descriptive model[J].Cement and Concrete Research,2005(6):1204-1209. |
[8] | A. Fernandez-Jimenez;A. Palomo .Composition and microstructure of alkali activated fly ash binder: Effect of the activator[J].Cement and Concrete Research,2005(10):1984-1992. |
[9] | Li Zongjin;Li Wenlai .Contactless,Transformer-based measure-ment of the resistivity of materials[P].US 6639401,2003-10-28. |
[10] | 魏小胜,肖莲珍,李宗津.采用电阻率法研究水泥水化过程[J].硅酸盐学报,2004(01):34-38. |