在惰性保护气氛中对TC4钛合金的激光快速成形进行了实验研究.研究结果表明,成形气氛中的氧含量,对成形工艺包括激光沉积工艺、成形表面质量、粉末利用率、熔覆层是否开裂等具有显著影响.氧含量严格控制在0.02%以下时,获得表面平整光洁、无裂纹等缺陷的TC4薄壁试样,粉末利用率达53%.
参考文献
[1] | J.Lin.Powder flow and catchment during coaxial laser cladding[A].,1999(3097):517-528. |
[2] | M Gremaud et al.[J].Surface Engineering,1996,12(03):251-259. |
[3] | M Gaumann.[J].Materials Science and Engineering A,1999(A271):232-241. |
[4] | J Mazumder.[J].Optics and Laser in Engineering,2000(34):397-414. |
[5] | D.M.Keicher.Using the laser engineered net shaping (LENS) process to produce complex components from a CAD solid model[A].,1995(2293):91-97. |
[6] | Arcella 等.[J].Journal of Metals,2000,52(05):28-30. |
[7] | C L Atwood et al.Laser spray fabrication for net-shape rapid product realization LDRD[R].Sandia Report,1999. |
[8] | Arcella.Rapid Laser Forming of Titanium Structures[A].Spain,1998 |
[9] | 陈静,杨海欧,张洪流,林鑫,李延民,黄卫东.Rene95高温合金的激光快速成形[J].钢铁研究学报,2003(z1):508-512. |
[10] | Yanmin Li.[J].Materials Science and Engineering,2003(A360):18-25. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%