通过仿生自组装法在室温下制备了纳米碳酸化羟基磷灰石/胶原(nCHAC)复合材料,并采用X射线衍射(XRD)、热分析(TGA)和透射电镜(TEM)进行了观察和分析.结果表明,该材料具有与天然骨相同的纳米尺度和胶原蛋白无机相,含有(2.8～14.7)w%的碳酸化HA成分;其显微结构是矿化的胶原纤维束,类似于天然骨的分级结构.揭示了碳酸化HA和胶原含量不同的复合材料中,具有微小差别的自组装单元.碳酸的百分含量影响矿物的晶体尺寸和胶原纤维的组装.因此,nCHAC复合材料是有前途的硬组织修复用材料,其所具有的特殊性能要归功于生物仿生制备出的nCHAC材料有与天然骨类似的成分和类似的微观结构.
参考文献
| [1] | Schanek W J;Yoshimura M .Processing and Properties of Hydroxyapatite-Based Biomaterials for Use as Hard Tissue Replacement implants [J].Journal of Materials Research,1998,13:94-117. |
| [2] | Doi Y;Shibutani T;Moriwaki Y et al.Sintered Carbonate Apatites as Bioresorbable Bone Substitutes[J].Journal of Materials Research,1998,39:603-610. |
| [3] | LeGeros R Z.Calcium Phosphates in Oral Biology and Medicine[M].Switzerland:Karger AG Press,1991 |
| [4] | Driessens F C M.Bioceramics of Calcium Phosphates[M].Boca Raton:crc Press,1983 |
| [5] | Tadic D;Epple M .A thorough physicochemical characterisation of 14 calcium phosphate-based bone substitution materials in comparison to natural bone.[J].Biomaterials,2004(6):987-994. |
| [6] | Zhang W.;Liao SS.;Cui FZ. .Hierarchical self-assembly of nano-fibrils in mineralized collagen[J].Chemistry of Materials,2003(16):3221-3226. |
| [7] | S.S.Liao;F.Z.Cui;Y.Zhu .Osteoblasts Adherence and Migration through Three-dimensional Porous Mineralized Collagen Based Composite: nHAC/PLA[J].Journal of Bioactive and Compatible Polymers,2004(2):117-130. |
| [8] | MDI JADE6 Software.XRD Pattern Processing[M].Materials Data,Inc,2003 |
| [9] | Peters F.;Epple M.;Schwarz K. .The structure of bone studied with synchrotron X-ray diffraction, X-ray absorption spectroscopy and thermal analysis[J].Thermochimica Acta: An International Journal Concerned with the Broader Aspects of Thermochemistry and Its Applications to Chemical Problems,2000(1/2):131-138. |
| [10] | Bradt J;Mertig M;Teresiak A et al.Biomimetic Mineralization of Collagen by Combined Fibril Assembly and Calcium Phosphate Formation[J].Chemistry of Materials,1999,11:2694-2701. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%