通过金相显微镜、扫描电镜和能谱仪等检测手段,对热轧生产线生产中出现的主要结疤类缺陷进行了归纳总结.结果表明:结疤类缺陷主要分为有焊接瘤压人类、转炉碱性渣卷入钢坯类、精炼渣卷入钢坯类及连铸坯气泡类等类型.在分析各类结疤缺陷的成因及影响因素的基础上,提出安装去毛刺设备,调整转炉炼钢及精炼过程和中间包冶炼制度,促进夹杂物上浮,制定合理钢包和中间包烘烤制度,检查结晶器装置是否渗水等相应的预防工艺措施.
参考文献
| [1] | 王中丙,谢利群,柴毅忠.CSP生产的热轧薄板边裂的影响因素与控制[J].钢铁,2002(09):31-34. |
| [2] | 刘运权,朱兴元,石俊.重轨结疤的产生与预防措施[J].上海金属,2008(03):45-48. |
| [3] | 彭凯,刘雅政,谢彬,周乐育,崔娟.热轧板结疤缺陷成因分析[J].钢铁,2007(03):44-46. |
| [4] | 韩郁文;李建新.连铸中间包钢液清洁度的研究[J].钢铁,1994(07):32. |
| [5] | Raihle C M .On the formation of pipes and centerline segregates in continuously cast billets[J].Met Traus,1994,25B:123. |
| [6] | Gabathuler J P .Fluid flow into a dendritic array under forced convection[J].Metallurgical and Materials Transactions,1983,14B:773. |
| [7] | Sivesson P .Improvement of inner quality of continuously cast billets through thermal soft reduction and use of multivariate analysis of saved process variables[J].Ironmaking and Steelmaking,1996,23(06):504. |
| [8] | 李积鹏,马杰,张有余.HP295焊瓶钢铸坯皮下气泡的成因分析及防止措施[J].中国冶金,2006(10):20-21,28. |
| [9] | 曾松盛,成小军,周明伟,梁武,王磊.Q345B热轧板板面结疤缺陷产生原因分析[J].中国冶金,2012(02):14-18,24. |
| [10] | 宋进英,董双鹏,陈业雄,张秉青,陈连生,田亚强.钢板边裂缺陷原因分析及整改措施研究[J].钢铁钒钛,2012(02):87-92. |
| [11] | 杨文,王新华,王万军,薛勇强,单庆林.一种热轧板表面长条线状缺陷的形成机理[J].钢铁钒钛,2011(03):34-39. |
| [12] | 滕涛,陈银莉,赵爱民,周欢,汪淑英.304不锈钢冷轧薄板表面线缺陷的形貌[J].钢铁钒钛,2007(03):28-32,50. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%