采用微弧氧化及水热合成处理方法制备钛合金表面生物膜层.应用扫描电子显微镜,EDS元素能谱及X射线衍射对薄膜的微观形貌、元素成分和相组成进行观察和分析,通过划痕试验检测膜基结合力,并研究试样在Hank's 模拟体液中耐腐蚀性能.将试样高温消毒后,分别植入至动物皮下组织,52 d后取出种植体并进行分析.结果表明:膜层与基体结合力可达26N左右,MAO-HS试样耐腐蚀性远强于基体试样;试验动物在试验过程中均未发生异常情况,微观形貌分析MAO-HS组试样发现膜层表面存在大量组织攀附,并含有一定比例的C、K元素.对照基体试样组,未见组织攀附.作为种植体材料,较基体合金MAO-HS试样表现出更为优异的组织相容性.
参考文献
| [1] | Yu Zhentao;Zhou Lian .Influence of martensitic transformation on mechanical compatibility of biomedical β type titanium alloy TLM[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2006(1/2):391-394. |
| [2] | 戚培毅,陈军,董汉山,况敏.医用钛材料表面改性及应用研究[J].材料研究与应用,2011(01):27-30. |
| [3] | Kakoli Das;Susmita Bose;Amit Bandyopadhyay .Smface modifications and cell-materials interactions with anodize Ti[J].ACTA BIOMATERIALIA,2007,3(04):573-585. |
| [4] | Xiaobing Luo;Li Zhang;Yos Morsi;Qin Zou;Yanying Wang;Shibo Gao;Yubao Li .Hydroxyapatite/Polyamide66 Porous Scaffold With An Ethylene Vinyl Acetate Surface Layer Used For Simultaneous Substitute And Repair Of Articular Cartilage And Underlying Bone[J].Applied Surface Science,2011(23):9888-9894. |
| [5] | Gagnon P .Improved antibody aggregate removal by hydroxyapatite chromatography in the presence of polyethylene glycol.[J].Journal of Immunological Methods,2008(2):222-228. |
| [6] | Gu YW;Khor KA;Pan D;Cheang P .Activity of plasma sprayed yttria stabilized zirconia reinforced hydroxyapatite/Ti-6Al-4V composite coatings in simulated body fluid.[J].Biomaterials,2004(16):3177-3185. |
| [7] | Svanborg LM;Hoffman M;Andersson M;Currie F;Kjellin P;Wennerberg A .The effect of hydroxyapatite nanocrystals on early bone formation surrounding dental implants.[J].International journal of oral and maxillofacial surgery,2011(3):308-315. |
| [8] | 高亚丽,接勐,张海波.医用镁合金表面激光重熔羟基磷灰石涂层[J].材料热处理学报,2012(09):117-121. |
| [9] | 骆海贺,蔡启舟,魏伯康,余博,何剑,李定骏.（NaPO3）6对AZ91D镁合金微弧氧化陶瓷层电化学腐蚀特性的影响[J].物理化学学报,2008(03):481-486. |
| [10] | 王亚明,蒋百灵,雷廷权,郭立新,曹跃平.电参数对Ti6Al4V合金微弧氧化陶瓷膜结构特性的影响[J].无机材料学报,2003(06):1325-1330. |
| [11] | 杜云慧,张鹏,王玉洁,郝志强.MB8镁合金的交流微弧氧化处理[J].无机化学学报,2012(10):2114-2120. |
| [12] | 刘忠德,严飞祥,孙茂坚,张中元,张仲谋.水热处理参数对Ti6Al4V合金微弧氧化膜HA生成的影响[J].轻金属,2011(04):50-54. |
| [13] | 郭恒,陈吉华,马楚凡,成炜.溶胶-凝胶/微弧氧化复合制备种植体表面HA/TiO2复合涂层的研究[J].中国美容医学,2007(03):394-397. |
| [14] | 刘杨,赵康,罗德福,汤玉斐.羟基磷灰石/二氧化钛生物复合涂层的制备及性能研究[J].西安理工大学学报,2008(02):220-223. |
| [15] | 马威,刘宝林,魏建华,王新木.微弧氧化处理后纯钛植入体的皮下埋置实验及表面元素成分研究[J].口腔医学研究,2004(04):376-378. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%