采用固溶强化、细晶强化和位错强化方法,模拟TSCR流程试开发高强度无取向电工钢,试开发钢的主要合金成分为3％ Si、0.83％A1和2.99％ Mn.分析热轧、常化、退火后的钢板组织,并针对不同的成品板组织,详尽地分析了相应的力学性能和磁性能.试验电工钢平均晶粒直径为12.37μm时,Rp0.2为530MPa,Rm为618MPa;当退火制度为700℃×4 min,成品组织完全为未再结晶的回复组织时,Rp0.22为853.5 MPa,Rm为895.5 MPa.该成分的电工钢P15/50或P10/400最小时,对应的平均晶粒直径都大于59.67μm;P10/800或P10/1000最小时,对应的平均晶粒直径都处于12.37～59.67 μm尺寸区间.
参考文献
| [1] | Seil Lee;B. C. De Cooman.Influence of Phosphorous and Boron on the Recrystallization, Grain Growth and Mechanical Properties of 3% Si steel[J].Materials Science Forum,2010:302-305. |
| [2] | Kabasawa A;Takahashi K .Development of the IMA motor for the V6 hybrid midsize sedan[J].SAE Transactions,2005,114(03):526-531. |
| [3] | Tanaka, I.;Yashiki, H. .Magnetic and Mechanical Properties of Newly Developed High-Strength Nonoriented Electrical Steel[J].IEEE Transactions on Magnetics,2010(2):290-293. |
| [4] | Park Hee Yong;Chang Sam Kyu;De Cooman Bruno .Development of high strength non-oriented electrical steels[J].The Minerals Metals & Materials Society,2008,3:247-250. |
| [5] | 田中一郎,屋铺裕义,岩本繁夫,高丸广毅,中山大成,李旭伦.资源节约型高强度电工钢SXRC的开发[J].钢铁研究学报,2011(06):63-66. |
| [6] | 谢晓心,张新仁.主要成分和工艺对极低铁损高磁感无取向电工钢磁性的影响[J].钢铁研究,2003(05):52-58. |
| [7] | 蒲春雷,李建军,岳尔斌,宋宁.CSP制无取向硅钢热轧、常化、冷轧织构的演变[J].钢铁钒钛,2012(03):65-69. |
| [8] | 黄璞,郭小龙,冯大军,杜光梁.无取向硅钢热轧组织演变规律的研究[J].武汉工程职业技术学院学报,2008(03):1-3. |
| [9] | 新日铁住金株式会社 .电工钢板[EB/OL].http://www.nssmc.com/product/catalog_download/pdf/D003jec.pdf,2012-10-05. |
| [10] | M.F. de Campos;J.C. Teixeira;F.J.G. Landgraf .The optimum grain size for minimizing energy losses in iron[J].Journal of Magnetism and Magnetic Materials,2006(1):94-99. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%