对一种钛微合金化Q345R容器钢的力学性能、显微组织和析出物进行试验研究,结果表明:Q345R含钛钢具有较高的强度性能、良好的延伸性和低温冲击韧性;其组织均以铁素体+珠光体组成,晶粒度约为12级;析出物为50 ～ 100 nm的TiN,开始析出温度为1 343℃,在固相线之下;计算表明微钛处理不足以形成TiC,细晶强化和固溶强化对强度的贡献最大.
参考文献
| [1] | 霍向东,毛新平,陈康敏,林振源.Ti含量对热轧带钢组织和力学性能的影响[J].钢铁钒钛,2009(01):23-28. |
| [2] | 毛新平.薄板坯连铸连轧微合金化技术[M].北京:冶金工业出版社,2008:67-162. |
| [3] | Xu Guang;Gan Xiaolong;Ma GuoJun et al.The development of Ti-allloyed high strength microalloy steel[J].Materials & Design,2010,31:2891-2896. |
| [4] | YI Hai-long,LIU Zhen-yu,WANG Guo-dong,WU Di.Development of Ti-Microalloyed 600 MPa Hot Rolled High Strength Steel[J].钢铁研究学报（英文版）,2010(12):54-58,64. |
| [5] | Xinping Mao;Xiangdong Huo;Xinjun Sun;Yizhong Chai .Strengthening mechanisms of a new 700 MPa hot rolled Ti-microalloyed steel produced by compact strip production[J].Journal of Materials Processing Technology,2010(12):1660-1666. |
| [6] | 王长军,雍岐龙,孙新军,毛新平,李昭东,雍兮.Ti和Mn含量对CSP工艺Ti微合金钢析出特征与强化机理的影响[J].金属学报,2011(12):1541-1549. |
| [7] | 雍岐龙;马鸣图;吴宝榕.微合金钢-物理和力学冶金[M].北京:机械工业出版社,1989:62-68. |
| [8] | 雍岐龙.钢铁材料中的第二相[M].北京:冶金工业出版社,2006:42-47. |
| [9] | 傅杰,朱剑,迪林,佟福生,柳得橹,王元立.微合金钢中TiN的析出规律研究[J].金属学报,2000(08):801-804. |
| [10] | 葛允宗,王建军,颜慧成,仇圣桃.含Ti齿轮钢中TiN夹杂析出热力学及其控制[J].钢铁钒钛,2012(05):50-54. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%