进行了6mm厚汽车新型钛合金Ti-6Al-4V-0.2Y板材的单面对接搅拌摩擦焊试验,并对接头的宏观形貌、X光无损探伤、显微组织、表面硬度和力学性能进行测试与分析.结果表明,钛合金Ti-6Al-4V-0.2Y板材的焊接接头成形好、表面光亮、无明显缺陷、力学性能较佳;接头的室温抗拉强度达到900 MPa、接头系数高达96％;接头硬度最大值位于焊核区、最小值位于前进侧热影响区.
参考文献
| [1] | L. Zhou;K. Nakata;J. Liao;T. Tsumura .Microstructural characteristics and mechanical properties of non-combustive Mg-9Al-Zn-Ca magnesium alloy friction stir welded joints[J].Materials & design,2012(Dec.):505-512. |
| [2] | Masayuki Aonuma;Kazuhiro Nakata .Dissimilar metal joining of ZK60 magnesium alloy and titanium by friction stir welding[J].Materials Science and Engineering B,2012,177:543-548. |
| [3] | 宋晓村,朱政强,陈燕飞.搅拌摩擦焊的研究现状及前景展望[J].热加工工艺,2013(13):5-7,12. |
| [4] | 吴超云,张津.基于专利文献的镁合金腐蚀与防护技术的最新进展[J].中国有色金属学报（英文版）,2011(04):892-902. |
| [5] | 吕赞,王琳,岳玉梅,姬书得,金延野.搅拌头压入速度和停留时间对2024铝合金搅拌摩擦焊接温度场的影响[J].热加工工艺,2013(01):171-173. |
| [6] | J. YANG;D. WANG;B.L. XIAO .Effects of Rotation Rates on Microstructure, Mechanical Properties, and Fracture Behavior of Friction Stir-Welded (FSW) AZ31 Magnesium Alloy[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2013(1):517-530. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%